Effect of Heat Treatment Process on Microstructure and Mechanical Properties of Cr8Mo2VSi and D2 Cold Work Steel

  • 马党参1,刘建华1,陈再枝1,康爱军2,迟宏宵1
Author information +
文章历史 +

摘要

研究了热处理工艺对高碳、高铬冷作模具钢Cr8Mo2VSi和D2钢的组织和性能的影响,结果表明:Cr8Mo2VSi比D2钢的碳化物更细小、均匀;1020~1040 ℃淬火,Cr8Mo2VSi的硬度略低于D2,经高温回火后,Cr8Mo2VSi钢表现出更好的二次硬化效应,其硬度高于D2钢1~2(HRC),并且比D2钢具有更好的强、韧性配合。

Abstract

The effect of heat treatment on the microstructure and mechanical properties of Cr8Mo2VSi and D2 cold work steels were investigated.The results show that carbides in Cr8Mo2VSi were more finer and distributed uniformly than in D2 steel.After heating at 10201040 ℃ then quenching in oil,Cr8Mo2VSi had lower hardness than that of D2 steel, but after tempering at higher temperature, secondary hardening of Cr8Mo2VSi was more obvious and Cr8Mo2VSi by 12HRC was harder than D2 steel, furthermore Cr8Mo2VSi had better combination of toughness and strength than D2.

关键词

冷作模具钢 / 淬火 / 回火 / 硬度 / 显微组织 / 冲击性能

Key words

cold work steel / quench / tempering / hardness / microstructure / impact property

图表

引用本文

导出引用
马党参, 刘建华, 陈再枝, . 热处理工艺对新型Cr8Mo2VSi和D2冷作模 具钢扁钢组织和力学性能的影响[J]. 钢铁, 2008, 43(9): 67-0
MA Dangshen, LIU Jianhua, CHEN Zaizhi, et al. Effect of Heat Treatment Process on Microstructure and Mechanical Properties of Cr8Mo2VSi and D2 Cold Work Steel[J]. Iron and Steel, 2008, 43(9): 67-0

Accesses

Citation

Detail

段落导航
相关文章

/