未再结晶固溶处理对无钴马氏体时效钢组织和拉伸性能的影响

  • 季长恩1，2,王威1，2，单以银1，杨柯1
作者信息 +

Influence of Unrecrystallization Solution Treatment on Microstructure and Tensile Properties of CobaltFree Maraging Steel

  • 季长恩1，2,王威1，2，单以银1，杨柯1
Author information +
文章历史 +

摘要

研究了未再结晶固溶处理对18Ni型无钴马氏体时效钢组织和拉伸性能的影响。研究结果表明，无钴马氏体时效钢经过未再结晶固溶处理后，马氏体形貌由块状转变为细小的条束状，拉伸断口上的韧窝明显变小变密；固溶态的硬度提高约3（HRC），抗拉强度提高约100 MPa；而时效态的硬度和强度提高幅度较小。

Abstract

Influence of unrecrystallization solution treatment on microstructure and tensile properties of 18Ni cobaltfree maraging steel was investigated. The experimental results showed that after unrecrystallization solution treatment，the morphology of martensites was changed from blocky to stringer, and the dimples on the tensile fracture became much finer； the hardness and tensile strength of the steel in solution condition increased by about HRC 3 and 100 MPa, respectively, but increased less for aged steel.

关键词

未再结晶固溶处理 / 无钴马氏体时效钢 / 显微组织 / 拉伸性能

Key words

unrecrystallization solution treatment / cobaltfree maraging steel / microstructure / tensile property

图表

引用本文

EndNote

Ris (Procite)

Bibtex

导出引用
季长恩, 王威, 单以银, 等. 未再结晶固溶处理对无钴马氏体时效钢组织和拉伸性能的影响[J]. 钢铁, 2008, 43(9): 75-0
JI Changen, WANG Wei, SHAN Yiyin, et al. Influence of Unrecrystallization Solution Treatment on Microstructure and Tensile Properties of CobaltFree Maraging Steel[J]. Iron and Steel, 2008, 43(9): 75-0

Accesses

Citation

Detail
段落导航
相关文章
月刊，1954年创刊
ISSN 0449-749X　CN 11-2118/TF
主　　管：中国科学技术协会
主　　办：中国金属学会
　　　　　钢铁研究总院有限公司
　　　　　北京钢研柏苑出版有限责任公司
主　　编：田志凌
编辑出版：北京钢研柏苑出版有限责任公司
国内发行：中国邮政集团有限公司北京市报刊发行局（邮发代号82-430）
　　　　　北京钢研柏苑出版有限责任公司
国外发行：中国国际图书贸易集团有限公司{北京399信箱)
地　　址：北京市海淀区学院南路76号（100081）
电　　话：010-62182345
E-mail：gangtiebianjibu@126.com
×

扫码分享

×

扫码分享

　版权所有 © 《钢铁》编辑部

/

〈 〉