摘要
对下游曲轴锻造厂提供的异议曲轴上的磁痕进行了着色渗透、磁粉探伤、金相和扫描电镜等系统检测，结合磁粉探伤的原理，阐明该磁痕属于发纹类磁痕，其本质是原材料中的一种硫化物偏聚现象，不会影响曲轴的使用性能。
Abstract
The magnetic particle indication appeared on objected crank shaft which provided by the downstream forging plant was systematically tested and analyzed by dye penetrant inspection， magnetic particle inspection， metallography inspection and scanning electron microscope analysis. Combined with the principle of magnetic particle inspection， it was concluded that the magnetic particle indication belonged to capillary crack， whose essence was one segregation phenomenon of sulfide， and it could not affect the service performance of crank shaft.
关键词
曲轴，磁痕，发纹
{{custom_keyword}} /
Key words
Crank Shaft, Magnetic Particle Indication, Capillary Crack
{{custom_keyword}} /
图表
刘桂江. , {{custom_author.name_cn}}等.
对45MnVS曲轴磁痕的检测分析[J]. 物理测试, 2018, 36(3): 5-8 https://doi.org/10.13228/j.boyuan.issn1001-0777.20170092
LIU Gui-Jiang. , {{custom_author.name_en}}et al.
Test and analysis of the magnetic particle indication of 45MnVS crank shaft[J]. Physics Examination and Testing, 2018, 36(3): 5-8 https://doi.org/10.13228/j.boyuan.issn1001-0777.20170092
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1].参考文献：
[2] 倪培相，孙军，周先忠，曲轴磁痕分析及其对疲劳强度的影响［J］.机械制造，2014，52（601）：64-66.
[3] 徐长林，张瑞卿等，钢材不同生产工艺对锻钢曲轴磁痕影响的探讨［J］.金属加工热加工，2013，23：48-49.
[4] 付翔.汽车转向节的锻造工艺［J］．锻压装备与制造技术，2012，47 ( 1) : 58-62．
[5] 刘必荣，小型柴油机曲轴表面缺陷磁粉探伤［J］.表面技术，2004，33（3）：67-68.
[6] 乔兵，汽车曲轴表面磁痕的形成原因［C］.西宁：2011 年全国高品质特殊钢生产技术研讨会，2011.
[7] 李爱娜，骆仕斌，曲轴锻造过程中的金属流动分析与磁痕研究 锻压技术［J］.2015 12（40）12-13
[8] 万建荣，刘子珍，余爱国.球墨铸铁曲轴表面荧光磁粉探伤［J］.汽车工艺与材料，2001（8）：39-41.
[9]吴成芸.浅议磁粉探伤中裂纹和发纹缺陷的磁痕特征[J].无损检测, 1999, 21(1):32-33
[10]徐高太，白淑娟，徐枭宇.曲轴磁痕分析[J].无损探伤, 2007, 31(6):47-48
[11] 张光华.相位角120°锻造曲轴探伤磁痕产生机理及减轻方法［D］.重庆：重庆大学，2011.
[12] 漆亮，第二轴立式模锻工艺研讨［J］.机械工人 热加工 2005，3：75.
[13] 冯继军，郭文芳，曾照鸿，48MnV非调质钢汽车发动机曲轴探伤磁痕现象分析及对疲劳性能的影想［J］，理化检验，2010，46（1）：44.
{{custom_fnGroup.title_cn}}
脚注
{{custom_fn.content}}