20Cr13 Stainless Steel Smelted by VOD Furnace Under Silicon Deoxidation Process
WANG Xin-chao1, YOU Zhi-min1, CHENG Guo-guang1, KOU Yu-shan2, ZUO Hui2, CHEN Lie2
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Xining Special Steel Co., Xining 810000, Qinghai, China
摘要 以实际工艺流程30 t EAF-VOD-LF-模铸冶炼20Cr13不锈钢为背景,通过热力学计算,对VOD精炼硅脱氧处理后,重新造渣过程中炉渣碱度、合金含量以及钢液温度对钢液中平衡氧含量的影响进行了研究。研究结果表明:钢液中的氧含量随炉渣碱度的增加呈现明显的减小趋势,实际生产中炉渣碱度一般应确保在2以上;为了保证添加合金进行脱氧的冶炼效果,应保证钢液中的硅的质量分数在0.3%以上;降低冶炼温度有利于降低钢液平衡氧含量;炉渣碱度对平衡溶解氧含量和实际生产全氧含量的影响规律基本相同,拟合出平衡溶解氧含量与实际全氧含量之间存在线性关系。
Abstract:Under the background 20Cr13 stainless steel smelted by 30 t EAF-VOD-LF-IC process, through thermodynamic calculation, effects of basicity, alloy content and steel temperature under the process of re-slag on the equilibrium oxygen content of liquid steel were studied after silicon deoxidation treatment in VOD refining process. The results show that the oxygen content is significantly decreased with the basicity of the slag increasing, the slag basicity should be in more than 2 in actual production. In order to ensure the smelting effect of adding alloy for deoxidation of liquid steel, It should ensure that the silicon content of 0.3% or more. With the temperature decrease, the equilibrium oxygen content in steel will decrease. Effects of slag basicity on the content of dissolved equilibrium oxygen content and the total oxygen content of actual production is basically in the same. A linear relationship between the content of dissolved equilibrium oxygen content and the total oxygen content of actual production was fitted.
收稿日期: 2013-08-22
出版日期: 2014-08-05
引用本文:
王鑫潮, 游志敏, 成国光, 寇玉山, 左 辉, 陈 列. VOD炉冶炼20Cr13不锈钢硅脱氧工艺[J]. 钢铁, 2014, 49(8): 31-34.
WANG Xin-chao, YOU Zhi-min, CHENG Guo-guang, KOU Yu-shan, ZUO Hui, CHEN Lie. 20Cr13 Stainless Steel Smelted by VOD Furnace Under Silicon Deoxidation Process. Iron and Steel, 2014, 49(8): 31-34.
Suzuki K, Ban-Ya S, Hino M. Deoxidation equilibrium of chromium stainless steel with Si at the temperatures from 1823 to 1923K [J]. ISIJ international, 2001, 41(8): 813-817.
[3]
Suzuki K, Ban-Ya S, Hino M. Deoxidation equilibrium of chromium stainless steel with Si at the temperatures from 1823 to 1923K [J]. ISIJ international, 2001, 41(8): 813-817.
[4]
Cha W Y, Kim D S, Lee Y D, et al. A thermodynamic study on the inclusion formation in ferritic stainless steel melt[J]. ISIJ international, 2004, 44(7): 1134-1139.
[4]
Cha W Y, Kim D S, Lee Y D, et al. A thermodynamic study on the inclusion formation in ferritic stainless steel melt[J]. ISIJ international, 2004, 44(7): 1134-1139.
[5]
Tsuneo Itoh, Tetsuya Nagasaka, Mitsutaka Hino. Equilibrium between Dissolved Chromium and Oxygen in Liquid High Chromium Alloyed Steel Saturated with Pure Cr2O3 [J]. ISIJ International, 2000, 40(11): 1051-1058.
[5]
Tsuneo Itoh, Tetsuya Nagasaka, Mitsutaka Hino. Equilibrium between Dissolved Chromium and Oxygen in Liquid High Chromium Alloyed Steel Saturated with Pure Cr2O3 [J]. ISIJ International, 2000, 40(11): 1051-1058.