Abstract:In order to explore the effect of heating rate and pre-melting on melting point and reveal the volatility characteristics of fluorine-containing slag at high temperature,a combined experiment of hemispherical melting point detection and thermogravimetry(TG)was taken. The melting point and volatilization characteristics of the fluorine-containing slag system were investigated under different heating rates and pre-melting processes. The results showed that the weight loss rate of fluorine-containing slag was 5%-17% during the melting point determination and it increased with the heating rate decreasing. There was almost no influence on the melting point of the fluorine-free slag before and after pre-melting,and for the fluorine-containing slag,the difference between the melting point of the mixed and the pre-melted slag was nearly 70 ℃. The reason for the difference was not the change of the phase composition,but the mixed slag had obvious volatilization. When is reached,the weight loss of the mixed slag was 8.3% at the melting point and that of the pre-melted slag was only 2%. There was a large amount of free CaF2 in the mixed slag sample,and for the pre-melted slag,CaF2 was mostly in the form of calcium fluoroaluminate and cuspidine. It provided a theoretical basis for exploring the effect of volatilization on high-temperature properties such as the melting point of fluorine-containing slag.
赵忠宇, 赵俊学, 谭泽馨, 屈波樵, 卢亮, 崔雅茹. 升温速率与预熔过程对含氟渣熔点影响分析[J]. 钢铁, 2020, 55(6): 123-128.
ZHAO Zhong-yu, ZHAO Jun-xue, TAN Ze-xin, QU Bo-qiao, LU Liang, CUI Ya-ru. Effect of heating rate and pre-melting process on melting point of fluorine-containing slag. Iron and Steel, 2020, 55(6): 123-128.
[1] 李正邦. 电渣冶金的理论与实践[M]. 北京:冶金工业出版社,2010. (LI Zheng-bang. Electroslag Metallurgy Theory and Practice[M]. Beijing:Metallurgical Industry Press,2010.) [2] 赵俊学,卢亮,赵忠宇,等. 电渣重熔用五元高氟渣高温挥发机制[J]. 钢铁,2019,54(6):43. (ZHAO Jun-xue,LU Liang,ZHAO Zhong-yu,et al. Volatilization mechanism of ESR slag with high fluoride under high-temperature[J]. Iron and Steel,2019,54(6):43. [3] 赵俊学,赵忠宇,尚南,等. 连铸保护渣中氟化物作用及影响分析[J]. 钢铁,2018,53(10):8. (ZHAO Jun-xue,ZHAO Zhong-yu,SHANG Nan,et al. Analysis on influence of fluoride in mold powder of continuous casting[J]. Iron and Steel,2018,53(10):8.) [4] 王哲,唐萍,米晓希,等. CaF2对CaO-SiO2-Al2O3渣系保护渣结晶行为的影响[J]. 钢铁,2018,53(7):38. (WANG Zhe,TANG Ping,MI Xiao-xi,et al. Effect of w((CaF2)) on crystallization properties of CaO-SiO2-Al2O3 based mold fluxes[J]. Iron and Steel,2018,53(7):38.) [5] ZHAO Jun-xue,ZHAO Zhong-yu,SHI Rui-meng,et al. Issues relevant to recycling of stainless-steel pickling sludge[J]. JOM,2018,70(12):2825. [6] 赵俊学,葛蓓蕾,崔雅茹. 含易挥发组元炉渣的高温性能检测[J]. 工业加热,2016,45(2):12. (ZHAO Jun-xue,GE Bei-lei,CUI Ya-ru,et al. High temperature properties measurement of slag with higher volatile content[J]. Industrial Heating,2016,45(2):12.) [7] 陈艳梅,赵俊学. 电渣冶金过程炉渣成分变化及其影响研究[J]. 工业加热,2014,43(3):23. (CHEN Yan-mei,ZHAO Jun-xue. Study on slag chemical composition change and its influence during ESR process[J]. Industrial Heating,2014,43(3):23.) [8] ZHAO Jun-xue,ZHAO Zhong-yu,CUI Ya-ru,et al. New slag for nickel matte smelting process and subsequent Fe extraction[J]. Metallurgical and Materials Transactions B,2018,49(1):304. [9] 梁洪铭,赵俊学,张振强,等. 电渣重熔过程炉渣中氟化物挥发的研究[J]. 特殊钢,2012,33(5):1. (LIANG Hong-ming,ZHAO Jun-xue,ZHANG Zhen-qiang,et al. A study on evaporation of fluorides in slag during electroslag remelting process[J]. Special Steel,2012,33(5):1.) [10] Shimizu K,Cramb A W. Fluoride evaporation from CaF2-SiO2-CaO slags and mold fluxes in dry and humid atmospheres[J]. High Temperature Materials and Processes,2003,22(5/6):237. [11] 陈艳梅,赵俊学,樊军,等. 电渣重熔过程中渣成分变化的研究[J]. 特殊钢,2010,31(6):7. (CHEN Yan-mei,ZHAO Jun-xue,FAN Jun,et al. A study on variations of slag ingredient during electroslag remelting proces[J]. Special Process,2010,31(6):7.) [12] 陈艳梅,赵俊学,路晓涛,等. CaF2渣系失重与成分变化的试验研究[J]. 钢铁研究学报, 2010,22(12):11. (CHEN Yan-mei,ZHAO Jun-xue,LU Xiao-tao,et al. Experimental study on weight loss and compositional variations of slag system bearing bearing CaF2[J]. Journal of Iron and Steel Research,2010,22(12):11.) [13] 巨建涛,吕振林,焦志远,等. CaF2-SiO2-CaO渣系的非等温挥发行为[J]. 过程工程学报,2012,12(4):618. (JU Jian-tao,LÜ Zhen-lin,JIAO Zhi-yuan,et al. Non-isothermal analysis on the evaporation behavior of CaF2-SiO2-CaO system slag[J]. The Chinese Journal of Process Engineering,2012,22(12):11.) [14] Mills K C. Physical properties of casting powders[J]. Ironmaking and Steeling,1988,15(4):175. [15] CHEN L Y,WEN G H,YANG C L,et al. Development of low-fluoride and titanium-bearing mould fluxes for medium carbon peritectic steel slab casting[J]. Ironmaking and Steelmaking,2015,42(2):105. [16] 茅洪祥,胡汉涛,马国军. 连铸保护渣对环境的氟污染及其对策[J]. 炼钢,1999,15(3):41. (MAO Hong-xiang,HU Han-tao,MA Guo-jun,et al. Contamination of fluorine in CC mould powder to environment and countermeasures[J]. Steelmaking,1999,15(3):41.) [17] 赵俊学,尚南,赵忠宇,等. 电渣重熔用中氟渣配渣方式对熔点测定的影响[J]. 钢铁,2018,53(8):44.(ZHAO Jun-xue,SHANG Nan,ZHAO Zhong-yu,et al. Influence of slag preparation mode on melting point of ESR slag with medium fluoride content[J]. Iron and Steel,2018,53(8):44.) [18] 赵俊学,王泽,赵忠宇,等. 氟化物挥发对连铸保护渣熔点的影响[J]. 钢铁,2019,54(8):181. (ZHAO Jun-xue,WANG Ze,ZHAO Zhong-yu,et al. Influence of fluoride evaporates on melting point of molding powder for continuous casting[J]. Iron and Steel,2019,54(8):181.