Abstract：Through plane strain compression ,the effect of distortion temperature on the hot ductility of 00Cr22Ni5Mo3N is studied ,and the dynamic softening mechanism of 00Cr22Ni5Mo3N duplex phases during hot distortion is investigated .The results show that the distortion temperature can markedly influence the peak stress of 00Cr22Ni5Mo3N specimens .And ferrite can be softened through dynamic restoration and recrystallization ，but austenite can be softened only through dynamic restoration during hot distortion .
宋志刚. 00Cr22Ni5Mo3N热变形动态软化机理研究[J]. 钢铁, 2009, 44(10): 61-61.
Song Zhi-gang. Research on dynamic softening mechanism of 00Cr22Ni5Mo3N during hot distortion. Iron and Steel, 2009, 44(10): 61-61.
2009, Vol. 44 