Effects of Tempering Temperature on Microstructure and Mechanical Properties for Q960 High-strength Structural Steel Plates
LU Feng1,2,KANG Jian1,WANG Chao1,WANG Zhao-dong1,WANG Guo-dong1
1. State Key Lab of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China 2. Wide Heavy Plate Project Manager Department of Tangshan Iron and Steel Corporation, Tangshan 063000, Hebei, China
Abstract：To develop the Q960 high-strength quenched and tempered structural steel plates, the effects of tempering temperature on the microstructure and mechanical properties of plate specimens were investigated on the same rolling and quenching conditions. The results show that with the increase of tempering temperature, the strength values of specimens are reduced, and the toughness and ductility show a mainly increasing tendency. But the temper brittleness appears at 300~450℃. The excellent overall properties of specimens with tempered sorbite can be obtained when the tempering temperature is 600℃, i.e., the yield strength is 1030MPa, tensile strength 1080MPa and percentage elongation 15.9% with the Charpy impact energy 144J at -40℃. All these indexes come up to the National Standard GB/T 16270-2009. Then the tensile behavior of specimens was discussed.
收稿日期: 2010-11-04
出版日期: 2012-02-20
引用本文:
卢峰,,康健,王超,王昭东,王国栋. 回火温度对Q960级高强结构钢组织及力学性能的影响[J]. 钢铁, 2012, 47(2): 92-95.
LU Feng1,2,KANG Jian1,WANG Chao1,WANG Zhao-dong1,WANG Guo-dong1. Effects of Tempering Temperature on Microstructure and Mechanical Properties for Q960 High-strength Structural Steel Plates. Iron and Steel, 2012, 47(2): 92-95.
2012, Vol. 47 