Abstract：The structure and properties of EAF slag and it’s leaching behavior of Cr were studied. The results indicate that the main minerals in the EAF slag are Ca2SiO4, Ca3Mg(SiO4)2 and MgCr2O4. The content of Cr2O3 in EAF slag is 2.92%.The slag are suitable for beneficial reuse, but metals in EAF slag are distributed evenly among every particle size. The leaching tests of Cr in slag show that the ratio of Cr leaching rate from slag in deionized water was inversely-proportional to particle size, and directly proportional to leaching time and liquid to solid ratio. Electromagnetic stirring improve the kinetic condition and improve Cr leaching rate. In deionized water, the percentage of Cr(Ⅵ) is higher than 50% in all the Cr leached from EAF slag. In acid solution, the volume of Cr leaching from slag increases but all the Cr are in the form of Cr（Ⅲ）.
收稿日期: 2011-12-13
出版日期: 2012-10-30
引用本文:
魏代修,徐安军,贺东风，田乃媛，杨泉. 电炉渣资源利用特性及铬的浸出特性[J]. 钢铁, 2012, 47(10): 92-96.
WEI Dai-xiu1,XU An-jun1,HE Dong-feng1,TIAN Nai-yuan1,YANG Quan2. Beneficial Reuse of EAF Slag and Its Leaching Behavior of Cr. Iron and Steel, 2012, 47(10): 92-96.
2012, Vol. 47 