Abstract：The hot metal with 0.06%-0.12% of w(［S］) was used for steelmaking at Pangang Extraction Vanadium and Steelmaking Plant. It’s difficult to product low sulfur steel. According with the practicing of the low sulfur steel of X52NS and L245NCS etc in Pangang, the sulfur content controlling technology was analyzed for the whole flow process including hot metal desulphurization pretreatment, converter ladle refining and continuous casting. Through controlling sulphur under 0.003% after the hot metal desulphurization pretreatment and using sulfur lower accessories slag in converter smelting station and molten steel LF station control ［O］ activity etc, Pangang Extraction Vanadium and Steelmaking Plant can produce the mass fraction of sulfur for 0.002% low sulfur steel.
收稿日期: 2012-12-27
出版日期: 2013-11-25
引用本文:
张强，袁宏伟，杨森祥，李清春，陈靓. 攀钢低硫管线钢硫含量控制生产实践[J]. 钢铁, 2013, 48(11): 32-36.
ZHANG Qiang，YUAN Hong-wei，YANG Shen-xiang，LI Qing-chun，CHEN Liang. Practice of Sulfur Content Control During the Smelting of Low Sulfur Pipeline Steel in Panzhihua Steel. Iron and Steel, 2013, 48(11): 32-36.
SOSINSKY DJ,KEMENY E I.Ladle slag control at rouge steel [J].Iron and Steel Maker,1992,9（7）：25~28
[4]
SOSINSKY DJ,KEMENY E I.Ladle slag control at rouge steel [J].Iron and Steel Maker,1992,9（7）：25~28
[5]
王新华，姜钧普，王福明.洁净钢—洁净钢生产工艺技术.北京：冶金工业出版社，2006.
[5]
王新华，姜钧普，王福明.洁净钢—洁净钢生产工艺技术.北京：冶金工业出版社，2006.
[6]
Coro Okuyama,Koji Yamaguchi,Syuji Takeuchi,et al.Effect of slag composition on the kinetics of formation of Al2O3-MgO inclusion in aluminum killed ferritic stainless Ssteel.ISIJ International,2000(2):121.
[6]
Coro Okuyama,Koji Yamaguchi,Syuji Takeuchi,et al.Effect of slag composition on the kinetics of formation of Al2O3-MgO inclusion in aluminum killed ferritic stainless Ssteel.ISIJ International,2000(2):121.
2013, Vol. 48 