High temperature mechanical property of SS400 B-bearing steel slab
WANG Wei,ZHOU Lü-min,XIONG Li,XUE Zheng-liang
(Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China)
Abstract:In order to avoid and reduce surface cracks of SS400 B-bearing steel slab, the high temperature mechanical properties of SS400 B-bearing steel slab have been investigated in the temperature range of 650-1 350 ℃ by the hot tensile test technique with Gleeble-1500 system. The results showed that its yield strength and tensile strength in the temperature range were relatively small;in general,which decreased with increased tested temperature. Only in the range of 1000-1 100 ℃,SS400 B-bearing steel slab has good hot ductility and the reductions of area were higher than 90%. The third brittle zone of the SS400 B-bearing steel is between 700-950 ℃. The low plasticity temperature range is relatively wide,because of boron segregation in grain boundaries and precipitation of BN leading to the grain boundary embrittlement. Because of the remelting phenomenon of B-bearing steel,the plasticity can be reduced when the temperature lies between 1 150-1 250 ℃.
王 炜,周律敏,熊 力,薛正良. SS400含硼钢连铸坯的高温力学性能[J]. 钢铁, 2015, 50(7): 38-42.
WANG Wei,ZHOU Lü-min,XIONG Li,XUE Zheng-liang. High temperature mechanical property of SS400 B-bearing steel slab. Iron and Steel, 2015, 50(7): 38-42.
Zhang D, Shintaku Y, Suzuki S, Komizo Y.In Situ Observation of Phase Transformation in Low-Carbon,Boron-Treated Steels[J].Metallurgical and Materials Transactions A, 2012, 43(2):447-458
[5]
Zhang D, Shintaku Y, Suzuki S, Komizo Y.In Situ Observation of Phase Transformation in Low-Carbon,Boron-Treated Steels[J].Metallurgical and Materials Transactions A, 2012, 43(2):447-458
[6]
Cho K C, Mun D J, Kim J Y.Effect of Boron Precipitation Behavior on the Hot Ductility of Boron Containing Steel[J].Metallurgical and Materials Transactions A, 2010, 41(6):1421-1428
[6]
Cho K C, Mun D J, Kim J Y.Effect of Boron Precipitation Behavior on the Hot Ductility of Boron Containing Steel[J].Metallurgical and Materials Transactions A, 2010, 41(6):1421-1428
[7]
Cho K C, Mun D J, Kang M H, Lee J S, Pank J K, Koo Y M.Effect of Thermal Cycle and Nitrogen Content on the Hot Ductility of Boron-bearing Steel[J].ISIJ International, 2010, 50(6):839-846
[7]
Cho K C, Mun D J, Kang M H, Lee J S, Pank J K, Koo Y M.Effect of Thermal Cycle and Nitrogen Content on the Hot Ductility of Boron-bearing Steel[J].ISIJ International, 2010, 50(6):839-846
[8]
Childs W J, Wilber G A.The Effects of Thermal History and Composition on the Hot Ductility of Low Carbon Steel[J].Metallurgical and Materials Transactions A, 1975, 6:1727-1735
[8]
Childs W J, Wilber G A.The Effects of Thermal History and Composition on the Hot Ductility of Low Carbon Steel[J].Metallurgical and Materials Transactions A, 1975, 6:1727-1735
[9]
Adams C J.Open Hearth and Basic Oxygen Steel [C]// Proceedings 49th National Chicago Meeting. Chicago: 1966.
[9]
Adams C J.Open Hearth and Basic Oxygen Steel [C]// Proceedings 49th National Chicago Meeting. Chicago: 1966.
[10]
张明如.连铸坯的组织与高温力学性能[J].马钢科技, 1996, 2:31-34
[10]
张明如.连铸坯的组织与高温力学性能[J].马钢科技, 1996, 2:31-34
[11]
Yin H, Blazek K, Lanzi O.In-situ” Observation of Remelting Phenomenon after Solidification of Fe–B Alloy and B-bearing Commercial Steels[J].ISIJ International, 2009, 49(10):1561-1567
[11]
Yin H, Blazek K, Lanzi O.In-situ” Observation of Remelting Phenomenon after Solidification of Fe–B Alloy and B-bearing Commercial Steels[J].ISIJ International, 2009, 49(10):1561-1567