高炉与KR双流程联动优化脱硫

doi:10.13228/j.boyuan.issn0449-749x.20160299

摘要
图/表
参考文献
相关文章 (15)

全文: PDF (0 KB) HTML (0 KB)
输出: BibTeX | EndNote (RIS)

摘要基于首钢京唐高炉工序与KR工序脱硫条件，对双流程的脱硫特点及经济性分别进行分析，发现焦炭为高炉硫负荷的主要来源。降低焦比或减少高硫炼焦煤的配比，是降低高炉硫负荷的有效措施，当铁水中[w(S)]由0.01%升高至0.05%时，高炉工序吨铁脱硫成本迅速下降，而当铁水中[w(S)]由0.06%变化至0.10%时，吨铁脱硫成本下降趋势变缓；KR脱硫吨铁成本随铁水中[w(S)]增加而逐渐升高。硫负荷为4 kg时，双流程综合脱硫成本最低时的铁水中[w(S)min]为0.067%，且[w(S)min]随硫负荷的增加而升高。当考虑炼焦配煤的采购成本时，由于硫质量分数高的炼焦配合煤采购成本较低，当采用高硫煤炼焦时，炼焦配煤带来的成本降低，不仅可以抵消由于双流程脱硫任务量增加而带来的成本增加，还可以使综合脱硫成本降低。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王振阳

关键词 ： Blast furnace, KR process, linkage, desulfurization

Abstract：Based on the desulfurization conditions of blast furnace and KR process in Shougang Jingtang， the characteristics and economical efficiency of the double processes were analyzed， respectively. The results showed that the main source of sulfur load for blast furnace was the coke， therefore the effective measures to reduce the BF sulfur load were decreasing the coke rate or the composition of coking coal with high sulfur contents. When the sulfur content in hot metal increased from 0.01% to 0.05%， the desulfurization cost per ton iron in BF process declined sharply. However， with the increase of[w(S)]from 0.06% to 0.10%， that cost in BF process decreased slightly. The spending of desulfurization in KR process grew steadily along with the increase of[w(S).] Under the condition of 4 kg sulfur load for BF， the desulfurization cost of the double-process was the lowest when the sulfur content of hot metal[w(S)min]was 0.067%. Moreover， the[w(S)min]rose with the sulfur load of BF. When considering the purchase cost of coking coal， the low cost of the coking coal with a high sulfur content not only counteracted the cost by the increasing desulfurization assignment， but also reduced the integrated desulfurization cost of the BF and KR processes.

收稿日期: 2016-07-06 出版日期: 2017-03-01

PACS:

TF535.2

引用本文:

王振阳，张建良，刘征建，张贺顺，安钢，程铮明. 高炉与KR双流程联动优化脱硫[J]. 钢铁, 2017, 52(2): 5-9. WANG Zhen-yang，ZHANG Jian-liang，LIU Zheng-jian，ZHANG He-shun，AN Gang，CHENG Zheng-ming. Joint-effect of blast furnace and KR on optimizing desulfurization. Iron and Steel, 2017, 52(2): 5-9.

链接本文:

http://www.chinamet.cn/Jweb_gt/CN/10.13228/j.boyuan.issn0449-749x.20160299 或 http://www.chinamet.cn/Jweb_gt/CN/Y2017/V52/I2/5

[1]	Shankar A. Sulphur partition between hot metal and high alumina blast furnace slag[J]. Ironmaking & Steelmaking, 2006, 33(5): 413-418.
[1]	Shankar A. Sulphur partition between hot metal and high alumina blast furnace slag[J]. Ironmaking & Steelmaking, 2006, 33(5): 413-418.
[2]	Wang Z Y, Zhang J L, An G, et al. Analysis on the Oversize Blast Furnace Desulfurization and a Sulfide Capacity Prediction Model Based on Congregated Electron Phase[J]. Metallurgical and Materials Transactions B-Process Metallurgy and Materials Processing Science, 2016, 47(1): 127-134.
[2]	Wang Z Y, Zhang J L, An G, et al. Analysis on the Oversize Blast Furnace Desulfurization and a Sulfide Capacity Prediction Model Based on Congregated Electron Phase[J]. Metallurgical and Materials Transactions B-Process Metallurgy and Materials Processing Science, 2016, 47(1): 127-134.
[3]	Lindstrom D, Sichen D. Study on Desulfurization Abilities of Some Commonly Used Desulfurization Agents[J]. Steel Research International, 2015, 86(1): 73-83.
[3]	Lindstrom D, Sichen D. Study on Desulfurization Abilities of Some Commonly Used Desulfurization Agents[J]. Steel Research International, 2015, 86(1): 73-83.
[4]	Xin T, Chushao X. Sulphur Distribution between CaO-SiO2-TiO2-Al2O3-MgO slag and Carbon-saturated iron at 1773K[J]. ISIJ International, 1995, 35(5): 367-371.
[4]	Xin T, Chushao X. Sulphur Distribution between CaO-SiO2-TiO2-Al2O3-MgO slag and Carbon-saturated iron at 1773K[J]. ISIJ International, 1995, 35(5): 367-371.
[5]	Wen M, Zhang T, Dou Z. Kinetics of Generation of Magnesium Vapor of Novel Magnesia-based Desulfurizer for External Desulfurization of Hot Metal[J]. ISIJ International, 2016, 56(1): 103-107.
[5]	Wen M, Zhang T, Dou Z. Kinetics of Generation of Magnesium Vapor of Novel Magnesia-based Desulfurizer for External Desulfurization of Hot Metal[J]. ISIJ International, 2016, 56(1): 103-107.
[6]	Ji J, Liang R, He J. Simulation on Mixing Behavior of Desulfurizer and High-sulfur Hot Metal Based on Variable-velocity Stirring[J]. ISIJ International, 2016, 56(5): 794-802.
[6]	Ji J, Liang R, He J. Simulation on Mixing Behavior of Desulfurizer and High-sulfur Hot Metal Based on Variable-velocity Stirring[J]. ISIJ International, 2016, 56(5): 794-802.
[7]	Magnelov M, Carlsson-Dahlberg A, Gustavsson L, et al. Iron losses during desulphurisation of hot metal utilising co-injection of Mg and CaC2 combined with nepheline syenite[J]. Ironmaking & Steelmaking, 2015, 42(7): 525-532.
[7]	Magnelov M, Carlsson-Dahlberg A, Gustavsson L, et al. Iron losses during desulphurisation of hot metal utilising co-injection of Mg and CaC2 combined with nepheline syenite[J]. Ironmaking & Steelmaking, 2015, 42(7): 525-532.
[8]	Lindstrom D, Du Sichen. Kinetic Study on Desulfurization of Hot Metal Using CaO and CaC2[J]. Metallurgical and Materials Transactions B-Process Metallurgy and Materials Processing Science, 2015, 46(1): 83-92.
[8]	Lindstrom D, Du Sichen. Kinetic Study on Desulfurization of Hot Metal Using CaO and CaC2[J]. Metallurgical and Materials Transactions B-Process Metallurgy and Materials Processing Science, 2015, 46(1): 83-92.
[9]	Nakai Y, Hino Y, Sumi I, et al. Effect of Flux Addition Method on Hot Metal Desulfurization by Mechanical Stirring Process[J]. ISIJ International, 2015, 55(7): 1398-1407.
[9]	Nakai Y, Hino Y, Sumi I, et al. Effect of Flux Addition Method on Hot Metal Desulfurization by Mechanical Stirring Process[J]. ISIJ International, 2015, 55(7): 1398-1407.
[10]	Vinoo D S, Mazumdar D, Gupta S S. Optimisation and prediction model of hot metal desulphurisation reagent consumption[J]. Ironmaking & Steelmaking, 2007, 34(6): 471-476.
[10]	Vinoo D S, Mazumdar D, Gupta S S. Optimisation and prediction model of hot metal desulphurisation reagent consumption[J]. Ironmaking & Steelmaking, 2007, 34(6): 471-476.
[11]	Kumar A, Chacko Z E, Malathi M, et al. Desulfurization of Hot Metal Through In Situ Generation of Magnesium in 30-kg Molten Iron Bath-Influence of Inert Gas Flow Rate[J]. Steel Research International, 2014, 85(5): 927-934.
[11]	Kumar A, Chacko Z E, Malathi M, et al. Desulfurization of Hot Metal Through In Situ Generation of Magnesium in 30-kg Molten Iron Bath-Influence of Inert Gas Flow Rate[J]. Steel Research International, 2014, 85(5): 927-934.
[12]	Lindstrom D, Nortier P, Du Sichen. Functions of Mg and Mg-CaO Mixtures in Hot Metal Desulfurization[J]. Steel Research International, 2014, 85(1): 76-88.
[12]	Lindstrom D, Nortier P, Du Sichen. Functions of Mg and Mg-CaO Mixtures in Hot Metal Desulfurization[J]. Steel Research International, 2014, 85(1): 76-88.
[13]	Liang N S. The technical and economic research on the sulfur contents in coke[J]. Lian Steel technology and management, 2014, (5): 43-47. [梁南山. 焦炭硫含量的技术经济研究. 涟钢科技与管理. 2014, (5): 43-47.]
[13]	Liang N S. The technical and economic research on the sulfur contents in coke[J]. Lian Steel technology and management, 2014, (5): 43-47. [梁南山. 焦炭硫含量的技术经济研究. 涟钢科技与管理. 2014, (5): 43-47.]