Fractal characterization of shear fracture interface of TA2/Q235 explosive composite plate under service environment
YANG Hong-bo1, KANG Jia1, GUO Long-chuang2, YAO Pei-wen1, LIU Huan1
1. School of Metallurgical Engineering, Xi′an University of Architecture and Technology, Xi′an 710055, Shaanxi, China; 2. BaoTi Group, Baoji 721003, Shaanxi, China
Abstract:In order to quantitatively study the relationship between shear strength and fractal dimension,and multifractal spectrum of TA2/Q235 explosive welded composite plate under service condition,and to identify the best fractal characterization method for TA2/Q235 composite plates,the service processes were simulated by heat treatment,shear experiments of the samples after service were carried out,and the fractal theory was introduced to characterize the shear fracture interface. The purpose of the above study is to establish the relation among shear strength,fractal dimension,and multiple fractal spectrums. The results show that after 200,400 and 600 ℃ service,the shear strength of the sample is negatively correlated with the width of the fracture multiple fractal spectrum. Combining with the analysis of the influence of residual stress elimination and recrystallization growth on shear fracture morphology of TA2/Q235 explosive composite plate,and comparing with fractal dimension,the multifractal spectrum can more accurately describe the mechanics′ information of fracture interface.
杨洪波, 康佳, 郭龙创, 姚沛文, 刘环. 服役环境下TA2/Q235爆炸复合板剪切断口分形表征[J]. 钢铁, 2020, 55(10): 115-119.
YANG Hong-bo, KANG Jia, GUO Long-chuang, YAO Pei-wen, LIU Huan. Fractal characterization of shear fracture interface of TA2/Q235 explosive composite plate under service environment[J]. Iron and Steel, 2020, 55(10): 115-119.
[1] 姜岳峰.TA2-316L爆炸焊接结合区硬化机理研究[D].沈阳:沈阳理工大学,2014.(JIANG Yue-feng. Investigation on Hardening Mechanism in the TA2/316L Explosive Welding Bonding[D]. Shenyang:Shenyang Ligong University,2014.) [2] Somasundaram Saravanan,Krishnamurthy Raghukandan,Kazuyuki Hokamoto. Improved microstructure and mechanical properties of dissimilar explosive cladding by means of interlayer technique[J]. Archives of Civil and Mechanical Engineering,2016,16:563. [3] 曹胜利,张庆军,朱立光,等. 基于多重分形研究脉冲磁场周期对凝固组织的影响[J]. 中国冶金,2019,29(4):31.(CAO Sheng-li,ZHANG Qing-jun,ZHU Li-guang,et al. Study on effect of pulsed magnetic field period on solidification structure based on multifractal method[J]. China Metallurgy,2019,29(4):31.) [4] 韩阳,杨晓磊,张欣,等. 镁质熔剂性球团矿相的多重分形谱[J]. 钢铁,2019,54(4):31.(HAN Yang,YANG Xiao-lei,ZHANG Xin,et al. Multifractal spectrum research of magnesia fluxing pellets[J]. Iron and Steel,2019,54(4):31.) [5] WANG Liang,WANG Li-dong,FEI Wei-dong. Fractal analysis of fracture surfaces in aluminum borate whisker-reinforced aluminum alloy 6061 composite[J]. Trans Nonferrous Met Soc China,2011(21):461. [6] WEI Tang,YONG Wang. Fractal characterization of impact fracture surface of steel[J]. Applied Surface Science,2012(258): 4777. [7] 付艳恕,张宾宾,夏萌. 铝-铝爆炸焊接界面剪切行为与断口形貌关系研究[J]. 实验力学,2015,30(2):165.(FU Yan-shu,ZHANG Bin-bin,XIA Meng. On the relationship between shear behavior and fracture morphology of 2024Al-Al explosive welding interfaces[J]. Journal of Experimental Mechanics,2015,30(2):165.) [8] 熊伟腾,范金娟,王云英,等. 材料断口分形维数测量方法研究进展[J]. 失效分析与预防,2019,14(1):66.(XIONG Wei-teng,FAN Jin-juan,WANG Yun-ying,et al. Progress of fractal dimension measurement method of material fracture[J]. Failure Analysis and Prevention,2019,14(1):66.) [9] 沈春豫,樊科社,李莹,等. 热处理工艺对爆炸焊接TA1/Q345R复合板残余应力分布影响[J]. 金属热处理,2019,44(8):205.(SHEN Chun-yu,FAN Ke-she,LI Ying,et al. Effect of heat treatment process on residual stress distribution of TA1/Q345R explosive welding clad plate[J]. Heat Treatment of Metals,2019,44(8):205.) [10] 姚沛文,杨洪波,刘环,等. 退火温度对TA2/Q235爆炸复合板组织性能的影响[J]. 金属热处理,2019,44(11):181. (YAO Pei-wen,YANG Hong-bo,LIU Huan,et al. Effect of annealing temperature on microstructure and properties of TA2/Q235 exploding welded composite plate[J]. Heat Treatment of Metals,2019,44(11):181.)