Abstract:The effect of Sn content on the corrosion resistance of a new type of lath martensitic low alloy ultra-high strength steel obtained by quenching and low temperature tempering in marine environment was studied by using 3.5%NaCl solution immersion test to simulate marine environment. The microstructure,mechanical properties and corrosion behavior of the two steels were studied by SEM,XRD,XPS,EPMA,electronic universal testing machine and pendulum impact testing machine. The evolution of the rust layer,phase composition and element distribution of test steel were analyzed. The result shows that the microstructure of two test steels with different Sn content after heat treatment is lath martensite. Meanwhile their comprehensive mechanical properties are excellent. Loose and easy-falling yellow-brown rust layer (NAR) of 0.042Sn test steel is formed on the surface during the immersion corrosion process. Due to the increase of Sn content in 0.2Sn test steel,brownish-black adhesive rust layer (AR) is gradually formed,which is attached to the surface of the substrate and close to the base. The rust layer of test steel presents an internal and external two-layer structure with the increase of corrosion time. The thickness of inner rust layer of 0.2Sn test steel gradually increases,which can effectively prevent corrosive ions from damaging the substrate. Fe,O and Cr are main elements of the rust layer at the initial stage of corrosion. Cr and Sn,the corrosion resistant elements,are enriched in layers in the inner rust layer at the middle and later stages of corrosion,which promotes the conversion of γ-FeOOH to α-FeOOH. The stable SnO2 oxidation products in the rust layer are highly protective,making the rust layer dense and uniform. FeCr2O4 and Cr(OH)3 block the penetration of Cl- and act as cation selective phase in the rust layer,thus improving the corrosion resistance of low alloy ultra-high strength steel.
林文丽, 邓想涛, 王麒, 周彦君, 王昭东. 锡对低合金高强钢海洋环境中腐蚀行为的影响[J]. 钢铁, 2023, 58(7): 113-124.
LIN Wenli, DENG Xiangtao, WANG Qi, ZHOU Yanjun, WANG Zhaodong. Effect of Sn on corrosion behavior of low-alloy high-strength steel in marine environment[J]. Iron and Steel, 2023, 58(7): 113-124.
[1] MORCILLO M,DÍAZ I,CANO H,et al. Atmospheric corrosion of weathering steels. Overview for engineers. Part I:Basic concepts[J]. Construction and Building Materials,2019,213:723. [2] 柯伟,董俊华. Mn-Cu钢大气腐蚀锈层演化规律及其耐候性的研究[J]. 金属学报,2010,46(11):1365.(KE W,DONG J H. Study on the rusting evolution and the performance of resisting to atmospheric corrosion for Mn-Cu steel[J]. Acta Metallurgica Sinica,2010,46(11):1365.) [3] 王进建,陈润农,胡惠超,等. 铝对4Cr1.5 Ni耐候钢组织和耐候性的影响[J]. 钢铁,2023,58(2):12.(WANG J J,CHEN R N,HU H C,et al. Effect of Al on microstructure and weathering resistance of 4Cr1.5 Ni weathering steel[J]. Iron and Steel,2023,58(2):12.) [4] DÍAZA I,CANO H,LOPESINO P,et al. Five-year atmospheric corrosion of Cu,Cr and Ni weathering steels in a wide range of environments[J]. Corrosion Science,2018,141:146. [5] NISHIMURA T. Rust formation and corrosion performance of Si- and Al-bearing ultrafine grained weathering steel[J]. Corrosion Science,2008,50:1306. [6] MA Y T,LI Y,WANG F H. Weatherability of 09CuPCrNi steel in a tropical marine environment[J]. Corrosion Science,2009,51:1725. [7] 高秀华,张大征,杜林秀,等. 低合金高强度抗应力腐蚀开裂海洋软管用钢的开发[J]. 轧钢,2019,36(4):1.(GAO X H,ZHANG D Z,DU L X,et al. Development of low-alloy high strength steel for marine flexible pipe with high resistance to stress corrosion cracking[J]. Steel Rolling,2019,36(4):1.) [8] 薛伟,李曌亮,余伟,等. 集装箱钢板在湿热海洋大气环境中的腐蚀行为[J]. 钢铁研究学报,2019,31(3):296.(XUE W,LI Z L,YU W,et al. Corrosion behaviors of container steel plates in tropical marine atmosphere environment[J]. Journal of Iron and Steel Research,2019,31(3):296.) [9] AHN S H,PARK K J,OH K N,et al. Effects of Sn and Sb on the corrosion resistance of AH32 steel in a cargo oil tank environment[J]. Metals and Materials International,2015,21(5):865. [10] PARDO A,MERINO M C,BOTELLA J,et al. Influence of Cu and Sn addition on the corrosion resistance of AISI 304 stainless steel in acid media[J]. Zeitschrift Für Metallkunde,2003,94(12):1339. [11] PARDO A,MERINO M C,CARBONERAS M,et al. Pitting corrosion behaviour of austenitic stainless steels with Cu and Sn additions[J]. Corrosion Science,2007,49:510. [12] NAM N D,KIM M J,JANG Y W,et al. Effect of tin on the corrosion behavior of low-alloy steel in an acid chloride solution[J]. Corrosion Science,2010,52:14. [13] LUO H,SU H Z,LI B S,et al. Electrochemical and passive behaviour of tin alloyed ferritic stainless steel in concrete environment[J]. Applied Surface Science,2018,439:232. [14] LIU B,MU X,YANG Y,et al. Effect of tin addition on corrosion behavior of a low-alloy steel in simulated costal-industrial atmosphere[J]. Journal of Materials Science and Technology,2019,35:1228. [15] SUN M H,YANG X J,DU C W,et al. Distinct beneficial effect of Sn on the corrosion resistance of Cr-Mo low alloy steel[J]. Journal of Materials Science and Technology,2021,81:175. [16] JIANG C,YANG Y,CHENG X Q,et al. Effect of Sn on the corrosion behavior of weathering steel in a simulated tropical marine atmosphere[J]. Anti-corrosion Methods and Materials,2020,67(2):129. [17] 黄小莉. 残余元素As、Sn、Sb的晶界偏聚对连铸钢热塑性的影响[D]. 武汉:武汉科技大学,2006.(HUANG X L. Effect of Grain Boundary Segregation of Residual Elements As,Sn and Sb on Thermo Plasticity of Continuous Casting Steel[D]. Wuhan:Wuhan University of Science and Technology,2006.) [18] 韩纪鹏,李阳,姜周华,等. 钢中低熔点元素的危害及含锡钢的发展研究[J]. 钢铁研究学报,2014,26(4):199.(HAN J P,LI Y,JIANG Z H,et al. Harmful effect of low-melting elements and development prospects of tin-containing steel[J]. Journal of Iron and Steel Research,2014,26(4):204.) [19] 刘珍光. 高浓度酸环境海洋软管铠装层用高强钢组织性能和腐蚀行为研究[D]. 沈阳:东北大学,2016.(LIU Z G. Study on the Microstructure and Mechanical Properties and Corrosion Behavior of Armor Layer Steel with High Strength of Oceanic Flexible Pipe at High-Concentration Acid Condition[D]. Shenyang:Northeastern University,2016.) [20] 黄涛,陈小平,王向东,等. 高强耐候钢在NaCl溶液中的腐蚀锈层特征和耐腐蚀性研究[J]. 机械工程学报,2017,53(20):45.(HUANG T,CHEN X P,WANG X D,et al. A study on the rust characteristics and corrosion resistance of high strength weathering steels in NaCl solution[J]. Journal of Mechanical Engineering,2017,53(20):45.) [21] GARCI′A K E,MORALES A L,BARRERO C A,et al. New contributions to the understanding of rust layer formation in steels exposed to a total immersion test[J]. Corrosion Science,2006,48(9):2813. [22] 姜杉,王瑞珍,侯清宇,等. 模拟流动海水腐蚀环境下含Cr钢与C钢的锈层研究[J]. 热加工工艺,2012,41(18):72.(JIANG S,WANG R Z,HOU Q Y,et al. Rust layer formed on Cr-containing steel and carbon steel in flow environment of artificial marine water[J]. Material and Heat Treatment,2012,41(18):72.) [23] 石云光,方圆,宋浩,等. 镀锡板在氯化钠溶液中的腐蚀行为研究[J]. 材料保护,2019(8) 69.(SHI Y G,FANG Y,SONG H,et al. Corrosion behavior of tinplate in NaCl solution[J]. Material Protection,2019(8):69.) [24] MA Y,LI Y,WANG F,et al. Corrosion of low carbon steel in atmospheric environments of different chloride content[J]. Corrosion Science,2009,51(5):997. [25] MA Y,LI Y,WANG F,et al. The effect of β-FeOOH on the corrosion behavior of low carbon steel exposed in tropic marine environment[J]. Materials Chemistry and Physics,2008,112(3):844. [26] NISHIMURA T,KATAYAMA H,NODA K,et al. Electrochemical behavior of rust formed on carbon steel in a wet/dry environment containing chloride ions[J]. Corrosion,2000,56(9):935. [27] ISHIKAWA T,KATOH R,YASUKAWA A,et al. Influences of metal ions on the formation of β-FeOOH particles[J]. Corrosion Science,2001,43(9):1727. [28] KAMIMURA T,HARA S,MIYUKI H,et al. Composition and protective ability of rust layer formed on weathering steel exposed to various environments[J]. Corrosion Science,2006,48(9):2799. [29] HUBBARD C R. RIR-measurement and use in quantitative XRD[J]. Powder Diffraction,1988,3:74. [30] JIANG S,CHAI F,SU H,et al. Influence of chromium on the flow-accelerated corrosion behavior of low alloy steels in 3.5% NaCl solution[J]. Corrosion Science,2017,123:217. [31] LUO H,YU Q,DONG C,et al. Influence of the aging time on the microstructure and electrochemical behaviour of a 15-5PH ultra-high strength stainless steel[J]. Corrosion Science,2018,139:185. [32] 杨颖,杨小佳,贾静焕,等. Sb和Sn微合金化对低合金钢在模拟污染海洋大气中腐蚀行为的影响[J]. 表面技术,2021,50(5):224.(YANG Y,YANG X J,JIA J H,et al. Effect of Sb and Sn on the corrosion behavior of low alloy steel in simulated polluted marine atmosphere[J]. Surface Technology,2021,50(5):224.) [33] 黄涛,王向东,陈小平,等. Sn-Sb耐候钢在模拟高湿热海洋大气环境中的耐蚀性研究[C]//2018第五届海洋材料与腐蚀防护大会暨海洋新材料及防护新技术展览会. [出版地不详]:中国腐蚀与防护学会,2018:133.(HUANG T,WANG X D,CHEN X P,et al. Corrosion resistance of Sn-Sb weathering steel in simulated high humidity-heat marine atmosphere[C]//The 5th Marine Materials and Corrosion Protection Conference and New Marine Materials and Protection Technology Exhibition in 2018. [S.L]:Chinese Cankerous and Protection Society,2018:133.) [34] 姜杉,王瑞珍,侯清宇,等. 模拟流动海水腐蚀环境下含Cr钢与C钢的锈层研究[J]. 热加工工艺,2012,41(18):72.(JIANG S,WANG R Z,HOU Q Y,et al. Rust layer formed on Cr-containing steel and carbon steel in flow environment of artificial marine water[J]. Material and Heat Treatment,2012,41(18):72.) [35] 王进建,刘静,陈润农,等. 海洋工程用9CrMo耐蚀钢筋组织及腐蚀行为[J/OL]. 钢铁[2023-01-16]. http://doi.org/10.13228/j.boyuan.issn0449-749x.20220610.(WANG J J,LIU J,CHEN R N,et al. Microstructure and corrosion behavior of 9CrMo corrosion-resistant steel bars for marine engineering[J/OL]. Iron and Steel[2023-01-16]. http://doi.org/10.13228/j.boyuan.issn0449-749x.20220610.) [36] KAMIMURA T,STRATMANN M. The influence of chromium on the atmospheric corrosion of steel[J]. Corrosion Science,2001,43(3):429. [37] 葛秋辰,汪兵,李远征,等. Sn对耐候钢高湿热海洋大气环境下耐蚀性能的影响[J]. 金属热处理,2017(2):67.(GE Q C,WANG B,LI Y Z,et al. Effect of Sn on corrosion resistance of weathering steel under marine atmosphere with high temperature and humidity[J]. Heat Treatment of Metals,2017(2):67.) [38] 陈健,陈玉鑫,黄涛,等. 不同铬含量耐候钢在高湿热模拟环境中的耐腐蚀性能[J]. 机械工程材料,2019,43(4):53.(CHEN J,CHEN Y X,HUANG T,et al. Corrosion resistance of weathering steels with different Cr content in simulated high temperature and humidity environment[J]. Materials for Mechanical Engineering,2019,43(4):53.)