Development status and prospects of bottom-blown O2-CaO technology in converter steelmaking process
DONG Kai1,2,3, WANG Chunyang1,2,3, ZHU Rong1,2,3, LIU Runzao2, REN Xin1,2,3, LIU Wenjuan4
1. Institute for Carbon Neutrality, University of Science and Technology Beijing, Beijing 100083, China; 2. Metallurgical and Ecological Engineering School, University of Science and Technology Beijing, Beijing 100083, China; 3. Beijing Key Laboratory of Special Melting and Preparation of High-End Metal Materials, Beijing 100083, China; 4. School of Advanced Engineering, University of Science and Technology Beijing, Beijing 100083, China
Abstract:In order to achieve green and clean production in BOF steelmaking and to meet the requirements of high scrap ratio smelting,the bottom-blown O2-CaO technology with metallurgical advantages such as high efficiency,cleanliness and low carbon has become a research hotspot. The development history and application status of bottom-blown O2-CaO technology in BOF steelmaking are summarized. The advantages of application in converter for high integration of control system,excellent metallurgical targets and low cost are presented in industrial applications. However,some problems are still existing which including short life for the bottom of furnace,the limited production cost advantages,small scale applications. Typical technologies including top and bottom blown converter steelmaking(K-BOP method),bottom blown CaO powder technology in top and bottom mixed blowing converter(K-OBM method),bottom-blown O2-CO2-CaO technology. The movable furnace bottom is used in K-BOP converter and K-OBM converter. The O2-CaO are sprayed into the furnace with multiple annulus bottom blowing elements,propane is blown into the annulus as cooling gas. The K-OBM method also achieves fully automatic smelting from charging to slag splashing,100% steel can be discharged without reversing the furnace. Consistency,high quality,high efficiency and low cost. The bottom-blown O2-CO2-CaO technology developed independently by USTB adopts fully automated smelting. The CO2 is mixed into O2 to take advantage of its heat absorption effect,weak oxidation,bubble multiplication and non-increasing nitrogen and hydrogen characteristics,to reduce the temperature of the bottom-blown fire-spot zone and extend the life of the bottom-blown components. It has the characteristics of high efficiency and clean,green and low carbon and low cost. In the end,we think about the development trend of the bottom-blown O2-CaO technology based on the low-carbon development strategy. And proposed that we should overcome erosion problems to match the safety and longevity smelting,expand the powder spraying function to meet the needs of low-carbon steelmaking,upgrade the automatic control system to adapt to the smelting of "Smart converter",analysis of the reaction mechanism of the bottom-blown O2-CO2-CaO converter to develop adapted process system. China′s bottom powder spraying technology will enter a period of vigorous development.
董凯, 王春阳, 朱荣, 刘润藻, 任鑫, 刘文娟. 转炉底吹O2-石灰粉技术的发展现状及展望[J]. 钢铁, 2023, 58(8): 13-24.
DONG Kai, WANG Chunyang, ZHU Rong, LIU Runzao, REN Xin, LIU Wenjuan. Development status and prospects of bottom-blown O2-CaO technology in converter steelmaking process[J]. Iron and Steel, 2023, 58(8): 13-24.
[1] 朱世海.喷射冶金的生产工艺与除杂特点[J].广西质量监督导报,2008(12):47.(ZHU S H.Production process and impurity removal characteristics of jet metallurgy[J]. Guangxi Quality Supervision Guide,2008(12):47.) [2] 张信昭.喷粉冶金基本原理[M].北京:冶金工业出版社,1988.(ZHANG X Z.Basic Principles of Powder Spraying Metallurgy[M].Beijing:Metallurgical Industry Press,1988.) [3] 胡绍岩.转炉炼钢长寿底吹氧气-石灰粉的应用基础研究[D].北京:北京科技大学,2019.(HU S Y.The Application Fundamental Research on Long-Life Bottom Blowing O2-CaO in Converter Steelmaking[D].Beijing:University of Science and Technology Beijing,2019.) [4] MARISSA V R,ANTONIO R S,RODOLFO M,et al.Hot metal pretreatment by powder injection of lime-based reagents[J].Steel Research,2001,72(5):173. [5] TSUTOMU N,SHUJI T,OSAMU H,et al.Mechanism of hot metal dephosphorization by injecting lime base fluxes with oxygen into bottom blown converter[J].Transactions of the Iron and Steel Institute of Japan,1983,23(6):513. [6] 赵斌,吴伟,吴巍,等. 不锈钢喷粉吹氧法铁水脱磷工艺[J]. 中国冶金,2022,32(6):155. (ZHAO B,WU W,WU W,et al. Dephosphorization process of hot metal by powder spraying and oxygen blow for stainless steel production[J]. China Metallurgy,2022,32(6):155.) [7] ZHOU Y,ZHU R,WEI G S.Application of submerged gas-powder injection technology to steelmaking and ladle refining processes[J].Powder Technology,2021,389:21. [8] KNUPPEL H,BROTZMANN K,FASSBINDER H G.Bottom-blown O converter:A new process for steelmaking[J].Stahl und Eisen,1973,93(22):1018. [9] 汪兴富.国内外氧气转炉技术的发展概况[J].重型机械,1988,1(14):1.(WANG X F.Overview of the development of oxygen converter technology at home and abroad[J].Heavy Machinery,1988,1(14):1.) [10] 邓开文.氧气底吹转炉的发展[J].钢铁,1979,14(4):61.(DENG K W.Development of oxygen bottom blowing converters[J].Iron and Steel,1979,14(4):61.) [11] KAWANA M,TSUTSUMIZAKI Y,NAGAI J,et al.Proceedings of the 95th conference of the iron and steel institute of Japan[J].Tetsu-to-Hagane,1978,64(4):166. [12] 汪兴富.日本川崎钢铁公司千叶厂的230吨氧气底吹转炉[J].重型机械,1978(6):115.(WANG X F.A 230 ton oxygen bottom blowing converter at the Chiba plant of Kawasaki Steel Company in Japan[J].Heavy Machinery,1978(6):115.) [13] 刘子明. 氧气底吹转炉在鞍钢平炉改造中应用的可能性[J]. 冶金能源,1982(4):1.(LIU Z M. The possibility of application of oxygen bottom blown converter in the transformation of open hearth furnace in Anshan Iron and Steel Co[J]. Energy for Metallurgical Industry,1982(4):1.) [14] TAOKA K.Smelting iron-body stainless steel in a ten bottom blow converter furnace[J].Tetsu-to-Hagane,1984,70(12):1027. [15] 李伟峰.转炉炼钢底吹O2-CO2-CaO脱磷应用基础研究[D].北京:北京科技大学,2021.(LI W F.Basic Research on Dephosphorization by Bottom Blowing O2-CO2-CaO in Converter Steelmaking[D].Beijing:University of Science and Technology Beijing,2021.) [16] 高柴信元,纪桂荣. 顶底吹转炉二次燃烧技术的开发[J]. 冶金能源,1989(6):51.(GAOCHAI X Y,JI G R. Development of secondary combustion technology of top and bottom blown converter[J]. Energy for Metallurgical Industry,1989(6):51.) [17] LIAO D S,SUN S,WATERFALL S.Integrated KOBM steelmaking process control[C]//The 6th International Congress on the Science and Technology of Steelmaking.Beijing:The Chinese Society for Metals,2015:12. [18] 李运平,刘卫东,李建民.提高K-OBM-S转炉炉衬寿命的措施[J].耐火材料,2006(1):69.(LI Y P,LIU W D,LI J M.Measures to improve the life of K-OBM-S converter lining[J].Refractory Materials,2006(1):69.) [19] 刘良春.喷射冶金技术的发展[J].钢铁研究,1988(3):93.(LIU L C.Development of jet metallurgy technology[J].Steel Research,1988(3):93.) [20] 关立华,齐世凯,邓开文.底吹氧气转炉喷粉冶炼含3%P高磷半钢[J].钢铁,1982,17(8):11.(GUAN L H,QI S K,DENG K W.Bottom-blown oxygen converter powder spraying smelting containing 3% P high phosphorus semi-steel[J].Iron and Steel,1982,17(8):11.) [21] 彭在美.马钢12吨氧气底吹转炉喷粉设备设计与试验研究[J].重型机械,1984(2):42.(PENG Z M.Design and experimental study of 12 ton oxygen bottom blowing converter powder spraying equipment of Magang[J].Heavy Machinery,1984(2):42.) [22] 野崎 努.底吹转炉法:引进·搅拌效果·顶底复合吹炼[M].北京:冶金工业出版社,2008.(NOZAKI T.Bottom Blowing Converter Method:Introduction,Stirring Effect,Top and Bottom Composite Blowing[M].Beijing:Metallurgical Industry Press,2008.) [23] ZHOU Y,ZHU R,HU S Y,et al.Study on metallurgical characteristics of the bottom-blown O2-CaO converter[J].Ironmaking and Steelmaking,2020,48(2):142. [24] 梁强,蔡俊.复吹转炉底吹氧气和石灰粉水模拟[J].钢铁,2020,55(5):26.(LIANG Q,CAI J.Water modeling experimenton bottom lime injection base fluxes with oxygen into combined blown converter[J]. Iron and Steel,2020,55(5):26.) [25] MORI T.International conference on basic oxygen steelmaking:A new technology emerges[J].Tetsu-to-Hagane,1978,64(14):2290. [26] 王学斌,冯明霞,刘崇林,等.复吹转炉底吹喷粉实验研究[J].材料与冶金学报,2009,8(1):12.(WANG X B,FENG M X,LIU C L,et al.Experimental study on blowing powder at the bottom of the re-blowing converter[J].Journal of Materials and Metallurgy,2009,8(1):12.) [27] 何洪声.冶金反应工程学在喷射冶金技术中的应用[J].云南冶金,2001,30(1):26.(HE H S.Application of metallurgical reaction engineering in jet metallurgy technology[J].Yunnan Metallurgy,2001,30(1):26.) [28] NOZAKI T,NAKANISHI K,MORISHITA H.Characteristics of dephosphorization in a bottom blown converter and its application to the preliminary treatment of hot metal[J].Tetsu-to-Hagane,1982,68(13):1737. [29] OHNISHI M,NAGAI J,YAMAMATO T,et al.Metallurgical characteristics and operation of top and bottom blowing oxygen converter at Mizushima works[J].Iron and Steelmaker,1983,(8):12. [30] 白丙中.转炉的K-OBM复吹工艺[J].鞍钢技术,1989(12):61.(BAI B Z.K-OBM re-blowing process for converters[J].Angang Technology,1989(12):61.) [31] HU S Y,ZHU R,LIU R Z,et al.Fluid-Solid coupling simulation on the temperature distribution of tuyere used for oxygen bottom blowing converter[J].Metallurgical and Materials Transactions B,2018,49(6):3317. [32] 高长春.氧气底吹熔炼氧枪浅析[J].中国有色冶金,2006(6):13.(GAO C C.Analysis of oxygen bottom blowing smelting oxygen gun[J].Chinese Nonferrous Metallurgy,2006(6):13.) [33] 刘凤霞.千叶钢厂1号炼钢车间顶底吹转炉用耐火材料的改进[J].国外耐火材料,1996(5):15.(LIU F X.Improvement of refractory materials in the first steelmaking workshop of Chiba Plant[J].Foreign Refractories,1996(5):15.) [34] LI W F,ZHU R,DONG K,et al.Physical simulation and industrial testing of bottom-blown O2-CaO converter for steelmaking process[J].Metallurgical and Materials Transactions B,2020,51(3):1060. [35] 普锐特冶金技术由BOF转炉升级成的KOBM转炉在河钢邯钢投入运行[EB/OL].世界金属导报 [2022-02-22].http://www.sohu.com/a/522320960_313737.(Primetals metallurgy's KOBM converter upgraded from BOF converter in operation at HISCO[EB/OL].World Metals[2022-02-22].http://www.sohu.com/a/522320960_313737.) [36] 潘秀兰.国内外转炉炼钢技术的新进展[J].鞍钢技术,2004(6):1.(PAN X L.New progress of converter steelmaking technology at home and abroad[J].Angang Technology,2004(6):1.) [37] HAN B C,WEI G S,ZHU R,et al.Utilization of carbon dioxide injection in BOF-RH steelmaking process[J].Journal of CO2 Utilization,2019,34:53. [38] ZHU R,HAN B C,DONG K.A review of carbon dioxide disposal technology in the converter steelmaking process[J].International Journal of Minerals,Metallurgy and Materials,2020,27(11):1421. [39] HU S Y,ZHU R,LIU R Z,et al.Decarburisation behaviour of high-carbon MgO-C refractories in O2-CO2 oxidising atmospheres[J].Ceramics International,2018,44(17):20641. [40] SU F Y,WEN Z.Hydraulic experiment on mushroom head in bottom-blown smelting furnace[J].Journal of Iron and Steel Research International,2017,24(5):490. [41] 杨利彬,曾加庆,邓勇,等.大型转炉高效率、长寿命顶底复合吹炼技术[J].钢铁,2020,55(4):45.(YANG L B,ZENG J Q,DENG Y,et al.High efficiency and long-life combined blowing technology of big converter[J].Iron and Steel,2020,55(4):45.) [42] 袁章福.转炉炼钢用煤技术的发展[J].江苏冶金,1988(1):36.(YUAN Z F. Development of coal technology for converter steelmaking[J].Jiangsu Metallurgy,1988(1):36.) [43] 张绍林.攀钢与卢森堡阿尔贝德公司转炉复吹技术交流[J].钢铁钒钛,1985(6):85.(ZHANG S L.Pangang exchanged converter blowing technology with Luxembourg Albede Company[J].Iron Steel Vanadium Titanium,1985(6):85.) [44] WIMMER G,PASTUCHA K,WIMMER E.Jet process for highest scrap rate in converter steelmaking[C]//The 6th International Congress on the Science and Technology of Steelmaking.Beijing:The Chinese Society for Metals,2015:140. [45] 朱荣,仇永全,万天骥,等.煤氧熔化废钢的试验研究[J].上海金属,1997,19(2):25.(ZHU R,QIU Y Q,WAN T J,et al.Experimental research on scrap melting in coal-oxygen furnace[J]. Shanghai Metals,1997,19(2):25.) [46] ERITZ E,PIRKLBAUER W,ZECHNER R,et al.The K-OBM and KMS converter for the flexible production of carbon and stainless steels and ferro-alloys[J].Steel Times International,1997,21(5):46. [47] 朱荣,任鑫,薛波涛.转炉炼钢工艺极限碳排放研究进展[J].钢铁,2023,58(3):1.(ZHU R,REN X,XUE B T.Research process of ultimate carbon emission in BOF steelmaking process[J].Iron and Steel,2023,58(3):1.) [48] KISHIMOTO Y,TAOKA K,TAKEUCHI S.Development of high-efficiency stainless steelmaking by Cr ore smelting reduction method[J].Kawasaki Steel Technical Report,1997(37):51. [49] TOMONO H.Development of steel continuous casting in Japan: Has Bessemer′s dream come true?[J].Ironmaking and Steelmaking,2015,42(4):242. [50] 张立峰.炼钢技术的发展历程和未来展望(Ⅱ):炼钢的未来展望[J].钢铁,2023,58(1):1.(ZHANG L F.Development history and future prospects of steelmaking(II):Future prospects[J].Iron and Steel,2023,58(1):1.)