Y15易切削钢孔洞分析及其预防
王维,赵四新,高加强
宝山钢铁股份有限公司中央研究院,上海 201999
Hole analysis of Y15 freecutting steel and its precautions
WANG Wei,ZHAO Sixin,GAO Jiaqiang
Research Institute, Baoshan Iron & Steel Co., Ltd., Shanghai 201999, China
摘要 采用体视显微镜(SM)、金相显微镜(OM)、扫描电子显微镜(SEM)及能谱仪(EDS)等对Y15易切削钢孔洞形成的原因进行了分析。结果表明,孔洞两边的裂纹呈应力裂纹特征,是最后一次热轧后方坯冷速过快所致,而孔洞则产生于随后的冷拔过程中。通过将方坯轧后空冷改为进缓冷坑缓冷后,制作的零件再无孔洞出现。
关键词 :
  ,
易切削钢 ,
冷拔 ,
孔洞
Abstract :The forming reactions of holes in Y15 freecutting steel were analyzed by stereomicroscope (SM), optical microscopy (OM), scanning electron microscope (SEM) and energy disperse spectroscopy (EDS). The results showed that the cracks on both sides of the hole had characteristics of stress cracking, which were caused by too fast cooling rate of the square billet after the last hot rolling. The hole was formed during the subsequent cold drawing process. By modifying the air cooling of the square billet to slow cooling in burial pit, no holes were found in the parts anymore.
Key words :
freecutting steel
colddrawing
hole
收稿日期: 2020-06-19
[1]
仇兵利1,随晖2,车德会3,孙铭山3,李建民3,王丽君1. 易切削不锈钢中氧含量和锻造比对硫化物形态及切削性能的影响 [J]. 钢铁研究学报, 2021, 33(5): 418-425.
[2]
李会朝,潘腾,程斌,张俊生. 700L热轧板材力学性能偏低分析与探究 [J]. 物理测试, 2021, 39(3): 7-.
[3]
彭进明,刘康康,柯鹏,宋强,章静. 椭圆孔型宽高比对线材表面变形状态的影响 [J]. 物理测试, 2021, 39(3): 13-.
[4]
赵同新,崔会杰,胡晓春,孙友宝,黄涛宏. 黄铜脱锌腐蚀行为特征的电子探针分析 [J]. 物理测试, 2021, 39(3): 23-.
[5]
燕顺,凌锐,唐振光,欧增微. 不锈钢原料内在缺陷致冷轧断带的分析与改进 [J]. 物理测试, 2021, 39(3): 38-.
[6]
Cheng-yang Hu, Hang-yu Dong, Kai-ming Wu, R.D.K. Misra, Lei Zhong, Xing Jin, Qiang Li. Zr脱氧对低杂质含量微合金厚板组织和力学行为的影响 [J]. 钢铁研究学报(英文版), 2021, 28(2): 190-200.
[7]
Hui Li, Li Feng, Hong Zhou, Peng Zhang, Ti Zhou, Qi Sui, Lu-quan Ren. 不同形式的仿生单元体对灰铸铁残余淬火表面修复的影响 [J]. 钢铁研究学报(英文版), 2021, 28(2): 201-210.
[8]
刘喜锚. 易切削钢连铸保护渣开发与应用 [J]. 连铸, 2021, 46(2): 66-70.
[9]
任桂香,晏德志,江在坤,孔武松,夏亚西. 石墨蠕化率对蠕墨铸铁受热变形趋势的影响 [J]. 物理测试, 2021, 39(2): 6-.
[10]
夏鹏,魏志辉. 基于电磁无损检测的车轮钢表面硬度检测方法 [J]. 物理测试, 2021, 39(2): 19-.
[11]
白克非,冯力伟. 重卡铸件、冲压焊接件锈蚀分析与改进 [J]. 物理测试, 2021, 39(2): 44-.
[12]
施虹屹,陈昌华,胡家豪,陈新华,刘昌乐. 实验室检测评定方法的测量不确定度 [J]. 物理测试, 2021, 39(2): 56-.
[13]
魏成革,张婷婷,马青军,张秋华. LNG储罐弹性毡拉伸强度测试及分析 [J]. 物理测试, 2021, 39(1): 19-.
[14]
董莎莎,李南,罗志强. 20CrMnMo减速机高速轴断裂原因分析 [J]. 物理测试, 2021, 39(1): 40-.
[15]
Run-sheng Xu, Shu-liang Deng, Heng Zheng, Wei Wang, Ming-ming Song, Wei Xu, Fang-fang Wang. Influence of initial iron ore particle size on CO2 gasification behavior and strength of ferro-coke [J]. 钢铁研究学报(英文版), 2020, 27(8): 875-886.