Kinetics of austenite grain growth in SCr420H steel
WANG Yang-xin1,2,ZHAO Xiu-ming1,2,MAO Xiang-yang1,2,BU Fan1,2,WANG Wan1,2,AN Jin-min3
(1. School of Material Engineering, Nanjing Institute of Technology, Nanjing 211167, Jiangsu, China 2. Jiangsu Key Laboratory of Advanced Structural Materials and Application Technology, Nanjing 211167, Jiangsu, China 3. Special Steel Research and Development Center of Research Institute, Baoshan Iron and Steel Co., Ltd., Shanghai 200940, China)
Abstract:The crystal growth behavior of SCr420H steel was studied. According to the solid solution formula of the second phase and the maximum the driving force of grain growth,the results were analyzed by the austenite grain size. Therefore,the result of SCr420H steel shows that the second phase particles are gradually reducing and the pinning effect weakly with the increase of holding temperature and the holding time. Grain growth is obvious,and grain size become coarsening gradually. Combined with the actual grain size and principle of Ostwald ripening growth in the second phase,the second phase dissolved less in the insulation 4 h conditions with the temperature rise,and the grain growth rate tends to slow to fast. Under the condition of temperature keeping in 5 and 6 h,the grain size grows steadily with the temperature increasing,and the speed of the growth tends to stop finally. When the holding temperature is above 1 020 ℃,the mixed crystal is more obvious. The initial grain size is 24 μm,and the grain growth of law accordance with Beck equation and Hillert grain growth law. The average activation energy of austenite grain growth is 564.6 kJ/mol.
Yan Y M, Liu Y Z, Zhou L Y, et al.Carburizing law and microstructure of 23CrNi3Mo drill steel[J].Cailiao Kexue Yu Gongyimaterial Science & Technology, 2013, 21(5):102-108
[1]
Yan Y M, Liu Y Z, Zhou L Y, et al.Carburizing law and microstructure of 23CrNi3Mo drill steel[J].Cailiao Kexue Yu Gongyimaterial Science & Technology, 2013, 21(5):102-108
[2]
Kundu A, Davis C L, Strangwood M.Pinning of Austenite Grain Boundaries by Mixed AlN and Nb(C, N) Precipitates[J]. Solid State Phenomena, 2011, 172-174: 458-463.
[2]
Kundu A, Davis C L, Strangwood M.Pinning of Austenite Grain Boundaries by Mixed AlN and Nb(C, N) Precipitates[J]. Solid State Phenomena, 2011, 172-174: 458-463.
[3]
Fang X.Effects of Grain Sizes and Second Phase Sizes of 16MnR Steel on Its Low Temperature Impact Toughness[J].Journal of Mechanical Engineering, 2011, 47(16):40-
[3]
Fang X.Effects of Grain Sizes and Second Phase Sizes of 16MnR Steel on Its Low Temperature Impact Toughness[J].Journal of Mechanical Engineering, 2011, 47(16):40-
Ding Zhimin, Fang Jianfei, Liang Bo, et al.Kinetics of austenite grain growth in V-Nb- (Ti) microalloyed steel[J].Journal of materials and heat treatment, 2013, 34(S1):88-92
[7]
Ding Zhimin, Fang Jianfei, Liang Bo, et al.Kinetics of austenite grain growth in V-Nb- (Ti) microalloyed steel[J].Journal of materials and heat treatment, 2013, 34(S1):88-92
Pan Xiaogang, Tang Di, Song Yong, et al.DP590 dual phase steel austenite grain growth model[J].Journal of University of Science and Technology Beijing, 2013, 35(2):189-194
[9]
Pan Xiaogang, Tang Di, Song Yong, et al.DP590 dual phase steel austenite grain growth model[J].Journal of University of Science and Technology Beijing, 2013, 35(2):189-194
Yu Shichang, Wu Shenqing, Gong Youjun, et al.Study on grain growth and dynamics of 6Cr21Mn10MoVNbN valve steel[J].iron and steel, 2006, 41(6):71-76
[11]
Yu Shichang, Wu Shenqing, Gong Youjun, et al.Study on grain growth and dynamics of 6Cr21Mn10MoVNbN valve steel[J].iron and steel, 2006, 41(6):71-76
[12]
Sugianto A, Narazaki M, Kogawara M, et al.Numerical simulation and experimental verification of carburizing-quenching process of SCr420H steel helical gear[J].Journal of Materials Processing Technology, 2009, 209(7):3597-3609
[12]
Sugianto A, Narazaki M, Kogawara M, et al.Numerical simulation and experimental verification of carburizing-quenching process of SCr420H steel helical gear[J].Journal of Materials Processing Technology, 2009, 209(7):3597-3609
[13]
Liu H Y, Liang Y C, Jin F F, et al.The research and Practice of reducing X80 pipeline steel mixed crystal structure[C]// asia steel international conference 2012.
[13]
Liu H Y, Liang Y C, Jin F F, et al.The research and Practice of reducing X80 pipeline steel mixed crystal structure[C]// asia steel international conference 2012.
[14]
Koura J, Tamaki M, Aramaki I, et al.Differences in water absorbency of polished rice and elasticity of steamed rice between large and small grains : Studies on the steamed rice in sake brewing (Part 3)[J].Journal of the Brewing Society of Japan, 2016, 105(9):597-603
[14]
Koura J, Tamaki M, Aramaki I, et al.Differences in water absorbency of polished rice and elasticity of steamed rice between large and small grains : Studies on the steamed rice in sake brewing (Part 3)[J].Journal of the Brewing Society of Japan, 2016, 105(9):597-603
Zhou Chao, Wang maoqiu, Dong Han, et al.The austenite grain growth kinetics of 38CrMoAl[J].steel, 2010, 45(12):73-76
[16]
Zhou Chao, Wang maoqiu, Dong Han, et al.The austenite grain growth kinetics of 38CrMoAl[J].steel, 2010, 45(12):73-76
[17]
Narita H, Tanaka M, Morisaku K, et al.Rapid Separation of Palladium(II) from Platinum(IV) in Hydrochloric Acid Solution with Thiodiglycolamide[J].Chemistry Letters, 2004, 33(9):1144-1145
[17]
Narita H, Tanaka M, Morisaku K, et al.Rapid Separation of Palladium(II) from Platinum(IV) in Hydrochloric Acid Solution with Thiodiglycolamide[J].Chemistry Letters, 2004, 33(9):1144-1145
[18]
Yang W, Gao F, Wei G, et al.Ostwald Ripening Growth of Silicon Nitride Nanoplates[J].Crystal Growth & Design, 2010, 10(1):29-31
[18]
Yang W, Gao F, Wei G, et al.Ostwald Ripening Growth of Silicon Nitride Nanoplates[J].Crystal Growth & Design, 2010, 10(1):29-31
Huang Shunzhe, Li Yong, Wang Chunxu, et al.Study on austenite grain growth law of 9310 steel[J].hot working technology, 2010, 39(18):31-33
[20]
Huang Shunzhe, Li Yong, Wang Chunxu, et al.Study on austenite grain growth law of 9310 steel[J].hot working technology, 2010, 39(18):31-33
[21]
Liu G Q, Yu H B, Song X Y, et al.Re-examination and extension of Hillert theory of two-dimensional normal grain growth[J].Medgenmed Medscape General Medicine, 2001, 9(4):632-638
[21]
Liu G Q, Yu H B, Song X Y, et al.Re-examination and extension of Hillert theory of two-dimensional normal grain growth[J].Medgenmed Medscape General Medicine, 2001, 9(4):632-638
[22]
Yang W Q, Min X U, Liang J X, et al.Non-equilibrium grain-boundary segregation of Bi in Cu bicrystals[J].Transactions of Nonferrous Metals Society of China, 2014, 24(12):4038-4043
[22]
Yang W Q, Min X U, Liang J X, et al.Non-equilibrium grain-boundary segregation of Bi in Cu bicrystals[J].Transactions of Nonferrous Metals Society of China, 2014, 24(12):4038-4043