Effect of TiN precipitation on hardenability in 20CrMnTi gear steel
LI Yao1, CHENG Guo-guang1, LU Jin-long1,2, SUN Jun3, HUANG Yu1
1. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing,Beijing 100083, China; 2. Technology Center, Baowu Group Guangdong Shaoguang Iron and Steel Co., Ltd., Shaoguan 512123, Guangdong, China; 3. Technology Center, Xinning SpecialSteel Co., Ltd., Xining 810005, Qinghai, China
Abstract:In order to study the effect of TiN precipitation on the hardenability in 20CrMnTi gear steel,based on the two kinds of end quenching specimens of 20CrMnTi steel with different hardenability characteristics come from the actual production,the peripheral hardness of the samples was tested,the microstructure and the austenite grain structure were observed by metallography microscope,the characteristics of TiN particles in steel were observed and analyzed by scanning electron microscopy,and the precipitation process of TiN was analyzed by Thermo-Calc software. The results show that the austenite grain size has a significant effect on the hardenability. The larger the grain size,the higher the martensite ratio,and the higher the hardness. The uniform and finer of the grain size reduces the maximum peripheral hardness difference of end-quenched samples from 9.1HRC to 3.3HRC. The precipitation of as much TiN as possible in the solid phase plays an important role in obtaining finer and uniform austenite grains. TiN precipitates out actually less during the solidification process and more in solid phase in the sample with better hardenability,which promotes grain refinement and more uniform peripheral hardness. In actual production,under the condition with specific mass percent of Ti,how to effectively inhibit the precipitation of TiN during solidification is the key to control narrow hardenability bandwidth for 20CrMnTi gear steel.
李尧, 成国光, 鲁金龙, 孙军, 黄宇. 20CrMnTi齿轮钢中TiN析出相对淬透性的影响[J]. 钢铁, 2021, 56(1): 75-84.
LI Yao, CHENG Guo-guang, LU Jin-long, SUN Jun, HUANG Yu. Effect of TiN precipitation on hardenability in 20CrMnTi gear steel[J]. Iron and Steel, 2021, 56(1): 75-84.
[1] 刘海宁,王郢,李仁兴,等. PMO凝固均质化技术在20CrMnTi齿轮钢上的应用[J]. 钢铁,2019,54(6):69.(LIU Hai-ning,WANG Ying,LI Ren-xing,et al. Application of pulse magneto-oscillation homogenization technique on continuous casting of 20CrMnTi gear steel[J]. Iron and Steel,2019,54(6):69.) [2] 王晓英,颜慧成,仇圣桃. 基于微观偏析模型的Mn-Cr系齿轮钢淬透性带宽[J]. 钢铁,2016,51(10):54.(WANG Xiao-ying,YAN Hui-cheng,QIU Sheng-tao. Hardenability bandwidth of Mn-Cr gear steel based on micro-segregation model[J]. Iron and Steel,2016,51(10):54.) [3] 刘锟,刘浏,何平,等. 齿轮钢窄淬透性带控制技术[J]. 钢铁,2015,50(3):73.(LIU Kun,LIU Liu,HE Ping,et al. Investigation on control technology of narrow hardenability band for gear steel[J]. Iron and Steel,2015,50(3):73.) [4] 易文. 20CrMnTiH(FQ)淬透性工艺研究[J]. 特钢技术,2012,18(2):27.(YI Wen. Research on hardenability of 20CrMnTiH(FQ) steel[J]. Special Steel Technology,2012,18(2):27.) [5] 吴季恂,周光裕,荀毓闽. 钢的淬透性应用技术[M]. 北京:机械工业出版社,1994.(WU Ji-xun,ZHOU Guang-yu,XUN Yu-min. Application Technology for Hardenability of Steel[M]. Beijing:China Machine Press,1994.) [6] 何肖飞,曹燕光,王毛球,等. 齿轮钢晶粒尺寸对淬透性的影响[J]. 钢铁研究学报,2018,30(3):206.(HE Xiao-fei,CAO Yan-guang,WANG Mao-qiu,et al. Effect of grain size on hardenability of gear steel[J]. Journal of Iron and Steel Research,2018,30(3):206.) [7] 申景霞,孙永喜,李法兴,等. Cr-Mn-Ti系齿轮钢添加硼元素的试验研究[J]. 钢铁,2012,47(1):24. (SHEN Jing-xia,SUN Yong-xi,LI Fa-xing,et al. Experimental study on adding boron in Cr-Mn-Ti gear steel[J]. Iron and Steel,2012,47(1):24.) [8] 张熹,王春旭,刘宪民,等. 化学成分波动对SAE9310钢淬透性和力学性能的影响[J]. 钢铁,2007,42(5):58.(ZHANG Xi,WANG Chun-xu,LIU Xian-min, et al. Effect of chemical composition fluctuation on hardenability and mechanical properties of SAE9310 steel[J]. Iron and Steel,2007,42(5):58.) [9] LIU S K,ZHANG G Y. The effect of Mn and Si on the morphology and kinetics of the bainite transformation in Fe-C-Ti alloys[J]. Metallurgical and Materials Transactions A,1990,21(6):1509. [10] 张健. 化学成分对20CrMnTi钢淬透性影响的研究[J]. 特钢技术,1998,1(1):36.(ZHANG Jian. Study on the effect of chemical composition on the hardenability of 20CrMnTi steel[J]. Special Steel Technology,1998,1(1):36.) [11] 史志强,李晶,余键,等. 20CrMnTi齿轮钢淬透性控制技术研究[J]. 炼钢,2008,24(6):47.(SHI Zhi-qiang,LI Jing,YU Jian,et al. Study on hardenability control of 20CrMnTi gear steel[J]. Steelmaking,2008,24(6):47.) [12] YANG Y H,WANG M Q,CHEN J C,et al. Microstructure and mechanical properties of gear steels after high temperature carburization[J]. Journal of Iron and Steel Research,International,2013,20(12):140. [13] Karmakar A,Kundu S,Roy S,et al. Effect of microalloying elements on austenite grain growth in Nb-Ti and Nb-V steels[J]. Materials Science and Technology,2014,30(6):653. [14] Mohrbacher H. Metallurgical concepts for optimized processing and properties of carburizing steel[J]. Advances in Manufacturing,2016,4(2):105. [15] Zhang L P,Davis C L,Strangwood M. Effect of TiN particles and microstructure on fracture toughness in simulated heat-affected zones of a structural steel[J]. Metallurgical and Materials Transactions A,1999,30(8):2089. [16] HUANG Y,CHENG G G,LI S J,et al. Effect of Ti(C,N) particle on the impact toughness of B-microalloyed steel[J]. Metals,2018,8(11):1. [17] 齐俊杰,黄运华,张跃. 微合金化钢[M]. 北京:冶金工业出版社,2006.(QI Jun-jie,HUANG Yun-hua,ZHANG Yue. Microalloyed Steel[M]. Beijing:Metallurgy Industry Press,2006.) [18] Maity S K,Ballal N B,Kawalla R. Development of ultrahigh strength steel by electroslag refining:Effect of inoculation of titanium on the microstructures and mechanical properties[J]. ISIJ International,2006,46(9):1361.