Abstract:According to its raw materials orthogonal test scheme is designed and a large number of systemic experiments were carried out in order to study the sintering characteristics of three types of fine ores in Kunming Iron&Steel Co.,Ltd(KISC). Expressions of mineral mixture average particle size and sintering tumble strength was obtained by analyzing the experimental data. The effects of carbon mixture ratio and basicity on FeO of sintering ore, agglomeration ratio, tunble strength and utilize coefficient were researched via single factor analysis and range analysis. The experimental results show the best mixture ratio of each fine ore. Analysis found that the influence of the carbon mixture ratio is more significant than which of the basicity on the sintering process except agglomeration ratio of foreign ore.
谢皓 白晨光 吕学伟 周传强 王 涛 王 凤. 昆钢铁矿粉烧结特性实验研究[J]. 钢铁, 2010, 45(2): 9-9.
XIE Hao . Sintering Characteristic Study of Fine Ores in KISC. Iron and Steel, 2010, 45(2): 9-9.