Investigation of Blooming of Austenitic Stainless Steel Ingot by ECAP
YANG Gang1, L Huisheng2,DENG Bo1,WANG Limin1,LIU Zhengdong1
1. Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China; 2. Department of Science and Technology Information, Central Iron and Steel Research Institute, Beijing 100081, China
Abstract:High temperature solution treatment of ECAPed samples of austenitic stainless steel ingot was studied experimentally , and both microstructure and properties of ECAP + solution samples were compared with that of forging + solid solution samples, the results show that full recrystallized microstructure of samples ECAPed at room and elevated temperature was obtained after solid solution at 1150 ℃.The increase of ECAP pass number has no effect on grain size, however homogeneity can be improved.After ECAP + solution treatment, both microstructure and properties of cast austenitic stainless steel samples are as same as that of forging + solution ones, showing that ECAP is a suitable method to replace blooming.
杨钢;吕惠生;邓波;王立民;刘正东. 用等径角挤压变形法进行奥氏体不锈钢锭开坯的研究[J]. 钢铁, 2008, 43(2): 77-0.
YANG Gang;L Huisheng;DENG Bo;WANG Limin;LIU Zhengdong. Investigation of Blooming of Austenitic Stainless Steel Ingot by ECAP. Iron and Steel, 2008, 43(2): 77-0.