Abstract：The study of secondary dendritic arm spacing(SDAS) in high carbon steel billets shows that the SDAS decreases with application of MEMS or increase with secondary cooling intensity, and the SDAS increases with increase of superheat and casting speed. The structure of columnar crystals is observed for billets cast without MEMS, and equiaxed structure for billets cast with MEMS, in which SDAS decreases obviously with increase of stirring current. The results indicate that the central carbon segregation of billets is aggravated with the increase of permeability due to enlarged SDAS.