Abstract:The change in mold flux composition, caused by the products (products of deoxidation and products of reoxidation as the results of chemical reactions on inner slagmetal interface, and inclusions from refractories) which were finally absorbed by mold flux, and its effects on flux properties were investigated by sampling mold flux during continuous casting of 304HC and analysis. By comparing these samples with the original flux, it was found that Al2O3 and Cr2O3 contents of mold flux were increased, F content was decreased and basicity of mold flux was reduced during casting. And all of these caused the change in properties of molten flux, such as viscosity, solidification temperature and the crystalline fraction of slag film. The results are good for the rational design of mold flux during casting of stainless steel and reducing the surface defects of stainless steel cast piece.
王新月;金山同. 不锈钢(304HC)浇铸过程保护渣成分变化及其对渣性能影响[J]. 钢铁, 2006, 41(11): 20-0.
WANG Xinyue;JIN Shantong. Change in Composition of Mold Flux and Its Effects on Properties During Casting 304HC Stainless Steel. Iron and Steel, 2006, 41(11): 20-0.