Abstract:The properties of inclusions in the welding wire steel and phases of caster nozzles were investigated by SEM, and the forming mechanism of the nozzle clogging was also studied by thermodynamic calculation. The results shows that large amounts of Al2O3 and TiO2 inclusions exist in the molten steel at the end of LF refining, and precipitates on the inner nozzles to form the clogging of alumina type, titania type, and two both individually, the continuous heats are merely 4. By optimizing the relationship of [Al]-[Ti]-[O] to make the content of w([Al]) above the equilibrium line between Al-Ti, w([Ti])/w([Al])4/3>84.49, and w([Ti])/w([Al])>7.46, when w([Al]) less than 0.0068%, the Al2O3 inclusions decrease obviously, the nozzle clogging can be efficiently reduced, and the continuous casting heats increase to 6.
Cramb A W, Jimbo I. Interfacial considerations in continuous casting [C]. Proc. of the W. O. Phibrook Memorial Symposium, Toronto, 1988, 259-271.
[10]
Cramb A W, Jimbo I. Interfacial considerations in continuous casting [C]. Proc. of the W. O. Phibrook Memorial Symposium, Toronto, 1988, 259-271.
[11]
Sasai K, Mizukami Y. Mechanism of alumina adhesion to continuous caster nozzle with reoxidation of molten steel [J]. ISIJ Int., 2001, 41(11): 1331-1339.
[11]
Sasai K, Mizukami Y. Mechanism of alumina adhesion to continuous caster nozzle with reoxidation of molten steel [J]. ISIJ Int., 2001, 41(11): 1331-1339.
[12]
Bernhard C, Xia G, Karasangabo A, Egger M, Pissenerger A. 超低碳钢连铸过程中Ti和P对水口结瘤的影响[J]. 世界钢铁,2012, (5): 19-24.
[12]
Bernhard C, Xia G, Karasangabo A, Egger M, Pissenerger A. 超低碳钢连铸过程中Ti和P对水口结瘤的影响[J]. 世界钢铁,2012, (5): 19-24.
[13]
Ogbayashi B. Mechanism and countermeasure of alumina buildup on submerged nozzle in continuous casting [J]. Taikabutsu Overseas, 1994, 15(1):3-14.
[13]
Ogbayashi B. Mechanism and countermeasure of alumina buildup on submerged nozzle in continuous casting [J]. Taikabutsu Overseas, 1994, 15(1):3-14.