LF精炼炉底吹CO2气体的工业探索性研究
谷云岭1,2 ,朱荣1,2 ,吕明1,2 ,陈列3 ,刘润藻1 ,尚大军3
1. 北京科技大学冶金与生态工程学院, 北京 100083 2. 北京科技大学钢铁冶金新技术国家重点实验室, 北京 100083 3. 西宁特殊钢股份有限公司, 青海 西宁 810005
Exploratory Research on Bottom Blowing CO2 During the LF Refining Process
GU Yun-ling1,2 ,ZHU Rong1,2 ,L Ming1,2 ,CHEN Lie3 ,LIU Run-zao1 ,SHANG Da-jun3
1. Metallurgical and Ecological Engineering School, University of Science and Technology Beijing, Beijing 100083, China 2. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China 3. Xining Special Iron and Steel Group Co., Ltd., Xi’ning 810005, Qinghai, China
摘要 基于LF精炼过程底吹CO2气体搅拌机制的研究,利用75t LF精炼炉进行底吹不同比例CO2与Ar混合气体的探索性工业试验。结果表明:底吹CO2气体使钢液搅拌增强,脱硫率由49.7%提高到65.1%,炉渣平均(FeO)质量分数均小于0.5%,满足精炼过程对炉渣氧化性的要求。钢液中夹杂物的种类、形貌和组成变化较小,夹杂物当量密度减小,钢液洁净度提高,试验表明LF炉可使用CO2气体进行精炼。
关键词 :
LF ,
二氧化碳 ,
脱硫 ,
洁净度
Abstract :The stirring mechanism of bottom blowing CO2 was investigated and some exploratory experiments were conducted with different proportion of CO2 during the 75t LF refining process in industry. The results show that bottom blowing CO2 can intensify liquid steel agitation and the desulfurization efficiency increases from 49.7% to 65.1%, the mass fraction of FeO is less than 0.5% in the slag so it can meet oxidizing requirements. Compared with bottom blowing Ar, the equal yield density of inclusions decreases and the cleanness of steel is improved, so it is possible for LF to use CO2.
Key words :
ladle furnace
CO2
desulphurization
cleanness
收稿日期: 2013-01-05
出版日期: 2013-08-19
引用本文:
谷云岭 ,朱荣 ,吕明 ,陈列,刘润藻,尚大军. LF精炼炉底吹CO2气体的工业探索性研究[J]. 钢铁, 2013, 48(8): 34-39.
GU Yun-ling,,ZHU Rong,,L Ming,,CHEN Lie,LIU Run-zao,SHANG Da-jun. Exploratory Research on Bottom Blowing CO2 During the LF Refining Process. Iron and Steel, 2013, 48(8): 34-39.
链接本文:
http://www.chinamet.cn/Jweb_gt/CN/ 或 http://www.chinamet.cn/Jweb_gt/CN/Y2013/V48/I8/34
[1]
刘仁生等.钢铁工业节能减排新技术5000问-炼铁系统分册.北京,中国科学技术出版社,2009:1.
[1]
刘仁生等.钢铁工业节能减排新技术5000问-炼铁系统分册.北京,中国科学技术出版社,2009:1.
[2]
柳克勋.关于钢铁企业发展低碳经济的思考.再生资源与循环经济,2010,3(4):11-15.
[2]
柳克勋.关于钢铁企业发展低碳经济的思考.再生资源与循环经济,2010,3(4):11-15.
[3]
张敬.中国钢铁行业CO2排放影响因素及减排途径研究.大连理工大学硕士学位论文.2008,12月.
[3]
张敬.中国钢铁行业CO2排放影响因素及减排途径研究.大连理工大学硕士学位论文.2008,12月.
[4]
宋士超.转炉顶底复合吹炼效果分析.炼钢,1986,1:54-58.
[4]
宋士超.转炉顶底复合吹炼效果分析.炼钢,1986,1:54-58.
[5]
郭木星,陈襄武.底吹CO2气体在复吹转炉熔池中的作用机理.钢铁研究学报,1993,5(1):9-14.
[5]
郭木星,陈襄武.底吹CO2气体在复吹转炉熔池中的作用机理.钢铁研究学报,1993,5(1):9-14.
[6]
野村宏之,森一美.Ar-CO2混合ガスㄧてよる溶鉄の脱炭反応機構.鉄と鋼,1972,12:49-57.
[6]
野村宏之,森一美.Ar-CO2混合ガスㄧてよる溶鉄の脱炭反応機構.鉄と鋼,1972,12:49-57.
[7]
野村宏之,森一美,城田良康.Ar-CO-CO2混合ガスㄧてよる溶鉄の脱炭反応.鉄と鋼,1974,3:39-49.
[7]
野村宏之,森一美,城田良康.Ar-CO-CO2混合ガスㄧてよる溶鉄の脱炭反応.鉄と鋼,1974,3:39-49.
[8]
R.D.O'Hara.Carbon Dioxide Shrouding and Purging at Ipsco'Melt Shop.I&SM,1986,3:24-28.
[8]
R.D.O'Hara.Carbon Dioxide Shrouding and Purging at Ipsco'Melt Shop.I&SM,1986,3:24-28.
[9]
John R. Paules.Ladle Stirring & Stream Shrouding with CO2 at Armco's Midwestern Steel Division.Steelmaking Proceeding,1987,129-132.
[9]
John R. Paules.Ladle Stirring & Stream Shrouding with CO2 at Armco's Midwestern Steel Division.Steelmaking Proceeding,1987,129-132.
[10]
T.BRUCE F.WEISANG M.ALLIBERT RFRUEHAN.Effects of CO2 Stirring In A Ladle. ELECTRIC FURNACE PROCEEDINGS.1987.293-297.
[10]
T.BRUCE F.WEISANG M.ALLIBERT RFRUEHAN.Effects of CO2 Stirring In A Ladle. ELECTRIC FURNACE PROCEEDINGS.1987.293-297.
[11]
张鉴.炉外精炼的理论与实践.冶金工业出版社,1999,6:233-238.
[11]
张鉴.炉外精炼的理论与实践.冶金工业出版社,1999,6:233-238.
[12]
森一美等.インジェクション冶金の動力学. 鉄と鋼,1981,6:672-695.
[12]
森一美等.インジェクション冶金の動力学. 鉄と鋼,1981,6:672-695.
[13]
陈建斌.炉外处理.冶金工业出版社,2008,10:155.
[13]
陈建斌.炉外处理.冶金工业出版社,2008,10:155.
[1]
Da‑peng Li, Hua‑zhang Wu, Hai‑feng Wang, Hong Li. Growth of solidified shell in bloom continuous casting mold of hypo-peritectic steel based on a FeS tracer method [J]. 钢铁研究学报(英文版), 2020, 27(7): 782-787.
[2]
闫学强1,2,郑万1,2,王国伟1,2,鄢文1,李光强1,2. 微孔MgO耐火材料对钢液洁净度的影响 [J]. 钢铁研究学报, 2020, 32(6): 483-490.
[3]
李晓源,时捷. 弹丸高速冲击条件下高强度钢板抗弹性能 [J]. 钢铁研究学报, 2020, 32(5): 429-436.
[4]
Jian-ming Su, Zhi-he Dou, Ting-an Zhang, Yan Liu. Kinetics of hot metal desulfurization by bottom blowing magnesium vapor [J]. 钢铁研究学报(英文版), 2020, 27(4): 392-401.
[5]
张威力1,吴胜利1,胡中杰1,2. 活性焦法烧结烟气脱硫率影响因素统计解析 [J]. 钢铁研究学报, 2020, 32(4): 281-288.
[6]
刘彭, 隋亚飞, 徐刚军, 周军军, 曾全文. 低碳钢夹杂物产生原因及控制 [J]. 钢铁, 2020, 55(2): 67-74.
[7]
印传磊, 杨丽梅, 田春阳, 马建超. KR铁水脱硫剂逸散及搅拌器黏渣分析 [J]. 钢铁, 2020, 55(1): 34-37.
[8]
陆亚男,吴胜利,王来信,寇明银. 炉渣成分对COREX铁水脱硫效果的影响 [J]. 钢铁, 2019, 54(9): 33-38.
[9]
肖尊湖,刘彭,徐刚军,周军军,隋亚飞. 不同钢种炉外精炼钙处理工艺的选择 [J]. 钢铁, 2019, 54(9): 62-72.
[10]
黄财德,何文远,刘延强,肖茂元,安泽秋,杨晓山. 电磁制动对镀锡板高拉速结晶器内流场的影响 [J]. 钢铁, 2019, 54(8): 90-101.
[11]
Ding Tian, Xiao-yi Shen, Yu-chun Zhai, Penny Xiao, Paul Webley. Extraction of iron and aluminum from high-iron bauxite by ammonium sulfate roasting and water leaching [J]. 钢铁研究学报(英文版), 2019, 26(6): 578-584.
[12]
刘纲 干勇 刘崇 马鸣图 朱荣 马浩冉. 低铝脱氧不锈钢夹杂物演变规律分析 [J]. , 2019, 44(6): 0-0.
[13]
Xiao-ming Li, Ming Lv, Wei-dong Yin, Jun-xue Zhao, Ya-ru Cui. Desulfurization thermodynamics experiment of stainless steel pickling sludge [J]. 钢铁研究学报(英文版), 2019, 26(5): 519-528.
[14]
林朝阳 朱德庆 郭正启. 废脱硫剂在铁矿烧结中的应用 [J]. 钢铁研究学报, 2019, 31(3): 272-279.
[15]
姚嘉斌 刘文果 巨建涛 邢相栋 安家良. CaO-SiO2-MgO-Al2O3-BaO渣系脱硫能力研究 [J]. 钢铁研究学报, 2019, 31(3): 280-286.