Influence of temperature on electrochemical corrosion
behavior of X80 pipeline and its weld joint XIE Fei1,XU Chang- hao1,WANG Dan1,WU Ming1,WANG Hai- yan1,XIE Hong- yu2
1. College of Petroleum Engineering,Liaoning Shihua University,Fushun 113001,Liaoning,China 2. Department of Inner Control,Petro China and NK Fuels Co. ,Ltd. ,Harbin 150000,Heilongjiang,China
Abstract:Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) technology were used to study the effect of temperature on electrochemical corrosion behavior of X80 pipeline steel and its weld joint in simulated Ku’erle soil solution. The results showed that the corrosion current density of X80 steel first increased and then decreased with the increase of temperature. Moreover,the increase of the amplitude gradually narrowed. When the temperature was 80 ℃,there was a peak value on charge transfer resistance,and the corrosion behavior of the metal was the most intense at this time. When the temperature was 90 ℃,electrode corrosion reaction was restrained,the corrosion rate decreased observably. The corrosion of weld joint part was more than other part of the steel at the same temperature.
谢飞,许长浩,王丹,吴明,王海燕,谢宏宇. 温度对X80管线钢及其焊缝腐蚀行为的影响[J]. 钢铁, 2015, 50(8): 89-94.
behavior of X80 pipeline and its weld joint XIE Fei,XU Chang- hao,WANG Dan,WU Ming,WANG Hai- yan,XIE Hong- yu. Influence of temperature on electrochemical corrosion. Iron and Steel, 2015, 50(8): 89-94.
Zazi N, Bouabdallah A, Aaboubi O, et al.Pretreatment effects on the electrochemical responses for aluminium–magnesium alloy AA5083 corrosion behavior[J].Journal of Solid State Electrochemistry, 2010, 14(9):1705-1711
[7]
Zazi N, Bouabdallah A, Aaboubi O, et al.Pretreatment effects on the electrochemical responses for aluminium–magnesium alloy AA5083 corrosion behavior[J].Journal of Solid State Electrochemistry, 2010, 14(9):1705-1711
[8]
Liu W.M.,Zhang HQ.,Qu Z.X.,et al. Corrosion behavior of the steel used as a huge storage tank in seawater[J].Journal of Solid State Electrochemistry, 2010, 14(6):965-973
[8]
Liu W.M.,Zhang HQ.,Qu Z.X.,et al. Corrosion behavior of the steel used as a huge storage tank in seawater[J].Journal of Solid State Electrochemistry, 2010, 14(6):965-973
[9]
Cheng Y.F.,Steward FR.. Corrosion of carborn steels in high temperature water studied by electrochemical techniques[J].Corrosion Science, 2004, 46(2):2405-2409
[9]
Cheng Y.F.,Steward FR.. Corrosion of carborn steels in high temperature water studied by electrochemical techniques[J].Corrosion Science, 2004, 46(2):2405-2409