Abstract：In order to study the effect of Na2O addition in basic slag on removal of phosphorus from SiMn alloys，dephosphorization thermodynamics of[w(P)]SiMn alloys （0.95%） at 1 400 ℃ was investigated by using CaO-SiO2-CaF2 slags， which contained small amounts of Na2O. The present study focused on the effect of small amounts of Na2O addition on the phosphorous distribution ratio between slags and alloys[(LP)，] the phosphide capacity of the slags[(CP)，] and the effect of basicity of the slags on[LP]with the replacement of CaO by Na2O. The results indicate that[LP]and[CP]increase with increasing [w(Na2O)；] when the[w(Na2O)]in the final slags is over 1.75%， both of them keep constant. The basicity of final slags increases with increasing the replacement of CaO by Na2O. However， when the basicity is over 3.655， namely， the replacement of CaO by Na2O is over 3.19%， the[O2－]concentration in the slags reaches saturation and[LP]keeps constant consequently.
周志强，朱子宗，丁羽川，周胜楠. Na2O对高磷硅锰合金脱磷的影响[J]. 钢铁, 2017, 52(4): 13-17.
ZHOU Zhi-qiang，ZHU Zi-zong，DING Yu-chuan，ZHOU Sheng-nan. Effect of Na2O on dephosphorization for high phosphorus SiMn alloys. Iron and Steel, 2017, 52(4): 13-17.
Zhu L J, Di W U, Zhao X M.Effect of Silicon Content on Thermodynamics of Austenite Decomposition in C-Si-Mn TRIP Steels[J].Journal of Iron & Steel Research International, 2006, 13(3):57-60
[1]
Zhu L J, Di W U, Zhao X M.Effect of Silicon Content on Thermodynamics of Austenite Decomposition in C-Si-Mn TRIP Steels[J].Journal of Iron & Steel Research International, 2006, 13(3):57-60
Ogasawara T, Ken-Ichi M, Tominaga T, et al.The Activity of Calcium in Calcium-Calcium Halide Fluxes[J]., 1996, 36:30-33
[3]
Ogasawara T, Ken-Ichi M, Tominaga T, et al.The Activity of Calcium in Calcium-Calcium Halide Fluxes[J]., 1996, 36:30-33
[4]
Masumitsu N, Ito K, Fruehan R J.Thermodynamics of Ca-CaF2 and Ca-CaCl2 systems for the dephosphorization of steel[J].Metallurgical Transactions B, 1988, 19(4):643-648
[4]
Masumitsu N, Ito K, Fruehan R J.Thermodynamics of Ca-CaF2 and Ca-CaCl2 systems for the dephosphorization of steel[J].Metallurgical Transactions B, 1988, 19(4):643-648
[5]
Tabuchi S, Sano N.Thermodynamics of phosphate and phosphide in CaO-CaF2 melts[J].Metallurgical & Materials Transactions B, 1984, 15(2):351-356
[5]
Tabuchi S, Sano N.Thermodynamics of phosphate and phosphide in CaO-CaF2 melts[J].Metallurgical & Materials Transactions B, 1984, 15(2):351-356
[6]
Shin J H, Park J H.Thermodynamics of Reducing Refining of Phosphorus from Si-Mn Alloy Using CaO-CaF2 Slag[J].Metallurgical & Materials Transactions B, 2012, 43(6):1-4
[6]
Shin J H, Park J H.Thermodynamics of Reducing Refining of Phosphorus from Si-Mn Alloy Using CaO-CaF2 Slag[J].Metallurgical & Materials Transactions B, 2012, 43(6):1-4
[7]
曾世林, 刘军, 李辉.锰硅合金炉外脱磷试验研究[J].铁合金, 2004, 35(1):1-5
[7]
曾世林, 刘军, 李辉.锰硅合金炉外脱磷试验研究[J].铁合金, 2004, 35(1):1-5
[8]
E.J. Jung, B.M. Moon, and D.J. Min.[J]., 2011, 95:1779-1779
[8]
E.J. Jung, B.M. Moon, and D.J. Min.[J]., 2011, 95:1779-1779
[9]
Pak J J, Fruehan R J.The effect of Na2O on dephosphorization by CaO-based steelmaking slags[J].Metallurgical & Materials Transactions B, 1991, 22(1):39-46
[9]
Pak J J, Fruehan R J.The effect of Na2O on dephosphorization by CaO-based steelmaking slags[J].Metallurgical & Materials Transactions B, 1991, 22(1):39-46
[10]
Kimura H, Tsukihashi F, Sano N.Thermodynamics of Na2O in the molten CaO-CaF2-SiO2 system[J].Metallurgical & Materials Transactions B, 1995, 26(26):553-556
[10]
Kimura H, Tsukihashi F, Sano N.Thermodynamics of Na2O in the molten CaO-CaF2-SiO2 system[J].Metallurgical & Materials Transactions B, 1995, 26(26):553-556
[11]
Aida E, Min D, Sano N.Phosphorus Distribution between Mn-Si Melts and CaO-SiO2-MnO-CaF2 Slags [J].Tetsu-to-Hagane, 1988, 74:1931-1938
[11]
Aida E, Min D, Sano N.Phosphorus Distribution between Mn-Si Melts and CaO-SiO2-MnO-CaF2 Slags [J].Tetsu-to-Hagane, 1988, 74:1931-1938
[12]
J.J. Pak.[J].Ph.D. Dissertation, 1987, :-
[12]
J.J. Pak.[J].Ph.D. Dissertation, 1987, :-
[13]
Aida E, Min D, Sano N.Phosphorus Distribution between Mn-Si Melts and CaO-SiO2-MnO-CaF2 Slags[J].Tetsu- to- Hagane, 1988, 74:1931-1938
[13]
Aida E, Min D, Sano N.Phosphorus Distribution between Mn-Si Melts and CaO-SiO2-MnO-CaF2 Slags[J].Tetsu- to- Hagane, 1988, 74:1931-1938
[14]
Ueda S, Morita K, Sano N.Thermodynamics of phosphorus in molten Si-Fe and Si-Mn alloys[J].Metallurgical & Materials Transactions B, 1997, 28(28):1151-1155
[14]
Ueda S, Morita K, Sano N.Thermodynamics of phosphorus in molten Si-Fe and Si-Mn alloys[J].Metallurgical & Materials Transactions B, 1997, 28(28):1151-1155
2017, Vol. 52 