Abstract:In order to further improve the strength and toughness and excellent corrosion resistance of super martensitic stainless steel,two new super martensitic stainless steels with nitrogen of 0.35% and manganese of 0.4% and 2.0%(mass percent) were developed and prepared under laboratory conditions,which are processed by quenching and partitioning process; The microstructure and mechanical properties of the steel were characterized by universal testing machine,optical microscope,scanning electron microscope,transmission electron microscope and electron backscattering diffraction. The results show that the mechanical properties of the two kinds of test steels are significantly improved compared with that of typical super martensitic stainless steels after quenching and partitioning. At the same time,it is found that manganese has a significant influence on the strength and toughness of the test steel. When the mass percent of manganese increases from 0.4% to 2.0%,the tensile strength and elongation of the test steel change from 1 690 MPa and 15.2% to 1 215 MPa and 35.1%,respectively,which both break the strength and toughness indexes of traditional super martensitic stainless steel. It is concluded that the reason for the significant improvement of strength and toughness is that the retained austenite content increases significantly after quenching and partitioning due to the synergistic effect of nitrogen and manganese,which is also caused by the precipitation of nano-scale reversed austenite and nitride.
庞阳, 邹德宁, 吕香, 李苗苗, 闫星宇. 锰对高氮超级马氏体不锈钢组织与性能的影响[J]. 钢铁, 2021, 56(3): 34-40.
PANG Yang, ZOU De-ning, LÜ Xiang, LI Miao-miao, YAN Xing-yu. Effect of manganese on microstructure and properties of high nitrogen super martensitic stainless steel[J]. Iron and Steel, 2021, 56(3): 34-40.
[1] 姜雯,赵昆渝,业冬,等. 热处理工艺对超级马氏体钢逆变奥氏体的影响[J]. 钢铁,2015,50(2):70.(JIANG Wen,ZHAO Kun-yu,YE Dong,et al. Effect of heat treatment technology on reversed austenite in super martensitic stainless steel[J]. Iron and Steel,2015,50(2):70.) [2] 陈肇翼,刘靖,任学平. 13Cr超级马氏体不锈钢热变形特性[J]. 中国冶金,2019,29(7):39.(CHEN Zhao-yi,LIU Jing,REN Xue-ping. Thermal deformation characteristics of 13Cr supermartensitic stainless steel[J]. China Metallurgy,2019,29(7):39.) [3] 张威,闫东娜,邹德宁,等. 超低碳13Cr-5Ni-2Mo马氏体不锈钢热变形行为及本构关系[J]. 钢铁,2012,47(5):69.(ZHANG Wei,YAN Dong-na,ZOU De-ning,et al. Hot deformation behavior and constitutive relationship for super-low carbon 13Cr-5Ni-2Mo martensitic stainless steel[J]. Iron and Steel,2012,47(5):69.) [4] Lee Y K,Shin H C,Leem D S,et al. Reverse transformation mechanism of martensite to austenite and amount of retained austenite after reverse transformation in Fe-3Si-13Cr-7Ni(wt.%) martensitic stainless steel[J]. Materials Science and Technology,2003,19(3):393. [5] Aquino J M,Della Rovere C A,Kuri S E. Localized corrosion susceptibility of supermartensitic stainless steel in welded joints[J]. Corrosion,2008,64(1):35. [6] Anselmo N,May J E,Mariano N A,et al. Corrosion behavior of supermartensitic stainless steel in aerated and CO2-saturated synthetic seawater[J]. Materials Science and Engineering A,2006,428(1/2):73. [7] 郭秀庭,任世举,彭雪梅,等. 大港油田高温深井试油套管强度校核[J]. 油气井测试,2019,28(6):38.(GUO Xiu-ting,REN Shi-ju,PENG Xue-mei,et al. Strength check of casing in high temperature deep well test in Dagang Oilfield[J]. Well Testing,2019,28(6):38.) [8] 罗懿,张传旭,金磊,等. 某油井L80钢油管腐蚀穿孔失效分析[J]. 理化检验-物理分册,2020,56(3):52.(LUO Yi,ZHANG Chuan-xu,JIN Lei,et al. Failure analysis on corrosion and perforation of L80 steel oil pipe of an oil well[J]. Physical Testing and Chemical Analysis Part A:Physical Testing, 2020,56(3):52.) [9] Speer J,Matlock D K,Cooman B C D,et al. Carbon partitioning into austenite after martensite transformation[J]. Acta Materialia,2003,51(9):2611. [10] 贾国翔,王存宇,宋文英,等. 一次淬火马氏体对Q&P钢组织和性能的影响[J]. 钢铁,2015,50(5):69.(JIA Guo-xiang,WANG Cun-yu,SONG Wen-ying,et al. Effects of initial quenched martensite on microstructure and mechanical properties of quenching and partitioning steel[J]. Iron and Steel,2015,50(5):69.) [11] 刘艳林. 一种Fe-C-Si-Mn-Cr-Mo钢碳配分行为对组织的影响[J]. 钢铁,2016,51(4):53.(LIU Yan-lin. Effect of carbon partitioning behavior on microstructure in a kind of Fe-C-Si-Mn-Cr-Mo steel[J]. Iron and Steel,2016,51(4):53.) [12] 李俊生,何方. 配分温度对于Q&P钢成形性的影响规律[J]. 中国冶金,2020,30(7):41.(LI Jun-sheng,HE Fang. Influence of partition temperature on formability of Q&P steel[J]. China Metallurgy,2020,30(7):41.) [13] 史园园,胡锋. 残留奥氏体对中碳双相钢冲击性能的影响[J]. 中国冶金,2015,25(1):21.(SHI Yuan-yuan,HU Feng. Effect of retained austenite on the impact properties in medium-carbon dual-phase steels[J]. China Metallurgy,2015,25(1):21.) [14] LU Si-yuan,YAO Ke-fu,CHEN Yun-bo,et al. Effect of quenching and partitioning on the microstructure evolution and electrochemical properties of a martensitic stainless steel[J]. Corrosion Science the Journal on Environmental Degradation of Materials and Its Control,2016,103:95. [15] Yuan L,Ponge D,Wittig J,et al. Nanoscale austenite reversion through partitioning,segregation and kinetic freezing: Example of a ductile 2 GPa Fe-Cr-C steel[J]. Acta Materialia,2012,60:2790. [16] SONG Yuan-yuan,CUI Jing-ping,RONG Li-jian. Microstructure and mechanical properties of 06Cr13Ni4Mo steel treated by quenching-tempering-partitioning process[J]. Journal of Materials Science and Technology,2016,32(2):189. [17] MA X P,WANG L,LIU C M,et al. Microstructure and properties of 13Cr5Ni1Mo0.025Nb0.09V0.06 N super martensitic stainless steel[J]. Materials Science and Engineering A—Structural Materials Properties Microstructure and Processing,2012(539):271.