Abstract：Vanadium-titanium magnetite is a mineral resource with great economic value and strategic significance. At present,its main processing method is the blast furnace-converter technology in current. This method has many disadvantages,such as high energy consumption,difficult operation and low resource utilization. There is an urgent need to develop a new extraction and separation technology valuable element for vanadium-titanium magnetite. OY furnace is a kind of melting reduction ironmaking process optimized based on COREX. It has the potential advantages of smelting vanadium-titanium magnetite such as pure O2 injection and lower burden load. The differences of softening and melting behavior of vanadium-titanium burden between blast furnace (BF) and OY furnace (OYF) were researched. The results showed that the softening shrinkage rate of DRI under OYF conditions was smaller duo to lower burden load than BF conditions. The DRI under OYF conditions was maintained a good morphology even at 1 450 ℃,and its temperature range of melting and dropping was declined by 79 ℃ compared with that in BF conditions. Moreover,the pressure drop of vanadium-titanium burden under blast furnace condition rises sharply twice due to the melting of slag and iron,and the foaming of slag,showing the characteristics of "multiple increases". The pressure drop of DRI under OYF conditions did not increase from melting to dropping,showing the characteristics of "single increases". Although the phenomenon of slag foaming appeared in the high temperature zone,namely dropping zone of both BF and OYF,the N2-free reducing atmosphere in the OYF inhibited the formation of high melting point phase Ti(C,N). The theoretical generation temperature of TiC in OYF is 1 481 ℃,the theoretical generation temperature of Ti(C,N) in BF is only 1 219 ℃. This study prove that the conditions of OYF improve the gas and liquid permeability of the vanadium-titanium burden,weaken the slag foaming,and are favorable for the smelting of vanadium-titanium magnetite.
尹铖, 张生富, 甘魏, 袁万能, 温良英, 白晨光. 高炉和欧冶炉条件下钒钛炉料软熔行为对比[J]. 钢铁, 2023, 58(8): 82-92.
YIN Cheng, ZHANG Shengfu, GAN Wei, YUAN Wanneng, WEN Liangying, BAI Chenguang. Differences of softening and melting behavior for vanadium- titanium burden under blast furnace and OY furnace conditions[J]. Iron and Steel, 2023, 58(8): 82-92.
[1] 张淑会,邵建男,毕忠新,等. 钒钛磁铁矿冶炼高炉喷吹焦炉煤气的减排能力[J]. 钢铁,2023,58(2):39.(ZHANG S H,SHAO J N,BI Z X,et al. Emission reduction ability of coke oven gas injection into blast furnace for smelting vanadium titanomagnetite[J]. Iron and Steel,2023,58(2):39.)
[2] 陈海彬,周振华,张作金,等. 钒钛磁铁矿综合回收研究进展[J]. 现代矿业,2023,39(1):7.(CHEN H B,ZHOU Z H,ZHANG Z J,et al. Research progress in the comprehensive recovery of vanadium-titanium magnetite[J]. Modern Mining,2023,39(1):7.)
[3] 白晨光,吕学伟,邱贵宝,等. 攀西钒钛磁铁矿资源高效冶金及清洁提取研究进展[J]. 过程工程学报,2022,22(10):1390.(BAI C G,LÜ X W,QIU B G,et al. Research progress on high efficiency metallurgy and clean extraction of vanadium-titanium magnetite ore in Panxi area[J]. Chinese Journal of Process Engineering,2022,22(10):1390.)
[4] 张树石,胡鹏,饶家庭,等. 钒钛磁铁矿综合利用现状及HIsmelt冶炼可行性分析[J]. 中南大学学报,2021,52(9):3085.(ZHANG S S,HU T,RAO J T,et al. Comprehensive utilization status of vanadium-titanium magnetite and feasibility analysis of HIsmelt smelting [J]. Journal of Central South University,2021,52(9):3085.)
[5] 王兴保. 基于3DMine软件的地质统计学在洋县毕机沟钒钛磁铁矿资源量计算中的应用[J]. 地质与勘探,2018,54(增刊1):1409.(WANG X B. Application of geostatistics based on 3DMine software to resource calculation of the Bijigou vanadium titanium magnetite deposit in Yangxian County,Shaanxi Province[J]. Geology and Exploration,2018,54(s1):1409.)
[6] 石煜,王玉往,王京彬,等. 新疆尾亚钒钛磁铁矿夕卡岩捕虏体的地质特征[J]. 矿产勘查,2021,12(4):883.(SHI Y,WANG Y W,WANG J B,et al. Geological characteristics of xenolith skarns in Weiya Fe-Ti-V oxide deposit,Xinjiang[J]. Mineral Exploration,2021,12(4):883.)
[7] TAYLOR P R,SHUEY S A,VIDAL E E,et al. Extractive metallurgy of vanadium-containing titaniferous magnetite ores:A review[J]. Mining,Metallurgy and Exploration,2006,23(2):80.
[8] HUKKANEN E,WALDEN H. The production of vanadium and steel from titanomagnetites[J]. International Journal of Mineral Processing,1985,15(1):89.
[9] 王勋,韩跃新,李艳军,等. 钒钛磁铁矿综合利用研究现状[J]. 金属矿山,2019,54(6):33.(WANG X,HAN Y X,LI Y J,et al. Research status on comprehensive development and utilization of vanadium-titanium magnetite[J]. Metal Mine,2019,54(6):33.)
[10] WANG B,DING X,JU T,et al. Influence of parameters on the pre-reduction process of vanadium-titanium magnetite carbon-containing composite pellets in Rotary Kiln[J]. Metals,2021,11(1):15.
[11] SUI Y,GUO Y,JIANG T,et al. Separation and recovery of iron and titanium from oxidized vanadium titano-magnetite by gas-based reduction roasting and magnetic separation[J]. Journal of Materials Research and Technology,2019,8(3):3036.
[12] 何佳,姜鑫,纪恒,等. 钒钛磁铁矿直接提钒的研究进展[J]. 中国冶金,2023,33(3):29.(HE J,JIANG X,JI H,et al. Research progress on direct extraction of vanadium from vanadium titanium magnetite[J]. China Metallurgy,2023,33(3):29.)
[13] 王海洋,张建良,王广伟,等. 八钢欧冶炉碱金属及锌平衡分析[J]. 炼铁,2018,37(4):61.(WANG H Y,ZHANG J L,WANG G W,et al. Analysis on balance of alkali metal and zinc in bayi steel′s OY furnace[J]. Ironmaking,2018,37(4):61.)
[14] 陈若平. 欧冶炉绿色炼铁生产实践[J]. 新疆钢铁,2019,25(4):44.(CHEN R P. Production practice of green ironmaking in the OY smelter[J]. Xinjiang Iron and Steel,2019,25(4):44.)
[15] HAN L,HUANG W,LIU Y. Effects of operation parameters on cohesive zone in corex melter gasifier[J]. ISIJ International,2016,56(9):1559.
[16] ZHOU X,DU Z. The introduction of COREX process development[J]. Advanced Materials Research,2013,774(9):1430.
[17] ZHOU X,SHI Z,ZHANG G,et al. Comparison of COREX and COSRI process technology development[J]. Applied Mechanics and Materials,2014,678(10):612.
[18] YOU Y,LUO Z,ZOU Z,et al. Numerical study on mixed charging process and gas-solid flow in COREX melter gasifier[J]. Powder Technology,2020,361(2):274.
[19] CHANG Z,ZHANG J,NING X. Phase and mineral behavior of coke in cohesive zone[J]. Fuel,2019,253:32.
[20] XIE H,YU W,YOU Z,et al. The effect of titanium carbonitride on the viscosity of high-titanium-type blast furnace slag[J]. Metals,2019,9(4):342.
[21] ZHANG L,YANG S,TANG W,et al. Effect of coke breeze content on sintering mechanism and metallurgical properties of high-chromium vanadium-titanium magnetite[J]. Ironmaking and Steelmaking,2020,47(7):821.
[22] JIAO L,KUANG S,YU A,et al. Three-dimensional modelling of an ironmaking blast furnace with a layered cohesive zone[J]. Metallurgical and Materials Transactions B,2020,51(1):258.
[23] MA K,XU J,DENG J,et al. Transient interaction between reduction and slagging reactions of wustite in simulated cohesive zone of blast furnace[J]. Metallurgical and Materials Transactions B,2018,49(5):2308.
[24] YU X,SHEN Y. Numerical study of the influence of burden batch weight on blast furnace performance[J]. Metallurgical and Materials Transactions B,2020,51(5):2079.
[25] ZHAO W,CHU M,LIU Z,et al. High-temperature interactions between vanadium-titanium magnetite carbon composite hot briquettes and pellets under simulated blast furnace conditions[J]. Metallurgical and Materials Transactions B,2019,50(4):1878.
[26] PAN Y Z,ZHANG A J,LIN L,et al. Correlation between reduction degree and softening and melting properties of pellets[C]//Proceedings of the 10th International Symposium on High-Temperature Metallurgical Processing. San Antonio:The Minerals,Metals and Materials Society,2019:523.
[27] 重庆大学. 一种高温连续变压、变气氛条件下铁矿石性能测定方法:中国,CN110346538B[P]. 2021-03-09[2023-06-09]. (Chongqing University. A Method for Measuring the Properties of Iron Ore under the Conditions of High Temperature Continuous Pressure Change and Variable Atmosphere:China,CN110346538B[P]. 2021-03-09 [2023-06-09].)
[28] ZHANG S F,BAI C G,ZHU R J,et al. A Method for Measuring Softening and Melting Performances of Iron Ore in Blast Furnace under Reducing Conditions with Variable Pressures:USA,US2021/0010753A1[P]. 2022-11-08 [2023-06-09].
[29] 中国国家标准化管理委员会. GB/T 34211—2017 铁矿石高温荷重还原软熔滴落性能测定方法[S]. 北京:中国标准出版社,2017.(China National Standardization Management Committee. GB/T 34211—2017,Iron ores:Method for Determination of Iron Reduction Softening Dripping Performance under Load[S]. Beijing:China standard Press,2017.)
[30] 宋家齐. 变压条件下钒钛烧结矿的高温还原软熔行为研究[D]. 重庆:重庆大学,2021.(SONG J Q. Study on Soft Melting Behavior of Vanadium Titanium Sinter in High Temperature Reduction under Variable Pressure[D]. Chongqing:Chongqing University,2020.)
[31] SRISHILAN C,SHUKLA A K. Static thermochemical model of corex melter gasifier[J]. Metallurgical and Materials Transactions B,2018,49(1):388.
[32] YIN C,ZHANG S,YANG X,et al. Smelting vanadium-titanium magnetite by corex process:Effect of V-Ti bearing pellet ratio on the softening and melting behavior of mixed burden[J]. Metallurgical and Materials Transactions B,2021,52:4096.
[33] PAL S,LAHIRI A K. Mathematical model of corex melter gasifier part 1 steady-state model[J]. Metallurgical and Materials Transactions B,2003,34B:103.
[34] YIN C,ZHANG S,GUO Y,et al. Effect of top gas recycling technology on the softening,melting and dropping behavior of V-Ti bearing burden in corex process[J]. ISIJ International,2022,62(9):1777.
[35] 沐继尧,毕学工,席更学. 熔滴实验结果鉴定指标的探讨[J]. 炼铁,1985,4(6):40.(MU J R,BI X G,XI G X,et al. Discussion on identification index of droplet test results[J]. Ironmaking,1985,4(6):40.)
[36] 陈立杰,柳政根,付小佼,等. 矿焦混装对钒钛矿综合炉料软熔滴落的影响[J]. 钢铁,2015,50(1):5.(CHEN L J,LIU Z G,FU X J,et al. Effects of ore-coke mixed charging on softening-dripping behavior of vanadium-titanium magnetite composite burdens[J]. Iron and Steel,2015,50(1):5.)
[37] 马家源,孙希文,盛世雄. 钒钛磁铁矿高炉冶炼的强化[J]. 钢铁,2000,35(1):4.(MA J Y,SHUN X W,SHENG S X,et al. Strengthening of blast furnace smelting of vanadium titanium magnetite[J]. Iron and Steel,2000,35(1):4.)
[38] 郄亚娜,靳亚涛,康媛,等. 高炉富氢对钒钛矿软熔滴落性能的影响[J]. 钢铁,2023,58(5):31.(QUE Y N,LE Y T,KANG Y,et al. Influence of hydrogen-rich on the softening and melting property of blast furnace burden with vanadium and titanium [J]. Iron and Steel,2023,58(5):31.)
[39] LIU Y X,ZHANG J L,ZHANG G H,et al. Influence of Ti(C0.3N0.7) on viscosity of blast furnace slags[J]. Ironmaking and Steelmaking,2017,44(8):609.
[40] WU K H,ZHANG G H,GOU H P,et al. Preparation and purification of titanium carbide via vacuum carbothermic reduction of ilmenite[J]. Vacuum,2018,151:51.
[41] 詹星. 小高炉冶炼钒钛磁铁矿解剖研究[J]. 钢铁钒钛,1984,5(2):3.(ZHAN X. Study on the anatomy of small blast furnace smelting vanadium-titanium magnetite[J]. Iron Steel Vanadium Titanium,1984,5(2):3.)
[42] 王耀祖,张建良,刘征建,等. w(TiO2)对烧结矿矿相结构及软熔滴落性能的影响[J]. 钢铁,2017,52(10):20.(WANG Y Z,ZHANG J L,LIU Z J,et al. Effects of w(TiO2) on mineral structure and softening-melting property of sinter[J]. Iron and Steel,2017,52(10):20.)
[43] 洪陆阔,齐渊洪,孙彩娇,等. 钒钛磁铁矿煤基直接还原试验[J]. 钢铁,2017,52(11):15.(HONG L K,QI Y H,SHUN C J,et al. Direct reduction of coal based vanadium-bearing titanomagnetite[J]. Iron and Steel,2017,52(11):15.)
2023, Vol. 58 