Abstract:In China,the steel slag production is large and stocks are high. Although hot recycling has been achieved in some enterprises,the phosphorus content in the slag has been continuously enriched and increased,and it is impossible to achieve secondary utilization fundamentally. In order to achieve the efficient leaching of phosphorus from high-phosphorus converter slag and reduce the loss of calcium oxide in the leaching process,different acid leaching schemes were designed. The effects of concentration,temperature,time,and stirring conditions of nitric acid and citric acid on the leaching effect were studied. At the same time,the optimal scale regression was used to analyze the test results. The results showed that the concentration of nitric acid had a great effect on leaching. If the citric acid was used at the same concentration of nitric acid,the loss of calcium oxide was low. Under the condition of no stirring at room temperature,the best acid leaching effect can be achieved by extending the acid leaching time. After leaching with citric acid and nitric acid,the CaSiO3 phase and Ca3(PO4)2-Ca2SiO4 phase in the slag disappeared successively. The optimal scale regression model had a good agreement with the experimental results. The use of selective leaching technology can create direct economic value and also bring indirect benefits to improve the ecological environment.
王仲亮, 包燕平, 王达志, 王敏. 高磷转炉渣中磷元素在不同酸中的浸出规律[J]. 钢铁, 2021, 56(4): 103-110.
WANG Zhong-liang, BAO Yan-ping, WANG Da-zhi, WANG Min. Leaching rule of phosphorus element in high phosphorus converter slag with different acids[J]. Iron and Steel, 2021, 56(4): 103-110.
[1] 薛保山.铁矿石消耗影响机制研究[D].北京:中国地质大学,2017.(XUE Bao-shan. Study on the Influence Mechanism of Iron Ore Consumption[D]. Beijing:China University of Geosciences,2017.) [2] 原材料工业司.2019年钢铁行业进出口情况[EB/OL].[2020-02-06].http://www.miit.gov.cn/n1146285/n11463 52/n3054355/n3057569/n3057572/c7639178/content.html.(Department of Raw Materials Industry. Import and Export Situation of Steel Industry in 2019[EB/OL]. [2020-02-06]. http://www.miit.gov.cn/n1146285/n1146352/n3054355/n3057569/n3057572/c7639178/content.html.) [3] 焦科诚.国外某高磷硅鲕状铁矿选矿工艺研究[J].矿冶工程,2018,38(4):65.(JIAO Ke-cheng. Study on the beneficiation process of a high-phospholious silicon oolitic iron ore abroad[J]. Mining and Metallurgical Engineering,2018,38(4):65.) [4] 王辉,张建松,孙瑞靖,等.高磷铁矿气化脱磷理论及试验研究[J].钢铁钒钛,2018,39(2):110.(WANG Hui,ZHANG Jian-song,SUN Rui-jing,et al. Theoretical and experimental study on dephosphorization of high-phosphorus iron ore gasification[J]. Iron and Steel Vanadium and Titanium,2018,39(2):110.) [5] 王臻,春铁军,李东升,等.高磷铁矿含碳团块直接还原动力学[J].过程工程学报,2018,18(3):530.(WANG Zhen,CHUN Tie-jun,LI Dong-sheng,et al. Kinetics of direct reduction of high-phosphate iron-bearing carbon-containing aggregates[J]. Journal of Process Engineering,2018,18(3):530.) [6] 林路,包燕平,王敏,等.二氧化钛改质对含磷转炉渣中磷富集行为的影响[J].北京科技大学学报,2014,36(8):1013.(LIN Lu,BAO Yan-ping,WANG Min,et al. Effect of titanium dioxide modification on phosphorus enrichment behavior in phosphorus-containing converter slag[J]. Journal of University of Science and Technology Beijing,2014,36(8):1013.) [7] 李瑞雪.钢渣混凝土发展的技术及经济评价研究[D].成都:西华大学,2018.(LI Rui-xue. Research on Technical and Economic Evaluation of Steel Slag Concrete Development[D]. Chengdu:Xihua University,2018.) [8] 李晨晓,赵定国,薛月凯,等.承钢半钢熔渣气化脱磷循环利用试验研究[J].炼钢,2019,35(4):19.(LI Chen-xiao,ZHAO Ding-guo,XUE Yue-kai,et al. Experimental research on recycling and dephosphorization of slag gasification and dephosphorization of Chenggang Steel[J]. Steelmaking,2019,35(4):19.) [9] 刘士琦,王书桓.转炉渣气化脱磷技术研究[J].河北冶金,2019(3):17.(LIU Shi-qi,WANG Shu-huan. Research on desulfurization technology of converter slag gasification[J]. Hebei Metallurgy,2019(3):17.) [10] 王书桓,郭瑞华,周朝刚,等.焦炭还原转炉熔渣气化脱磷研究[J].钢铁钒钛,2019,40(5):138.(WANG Shu-huan,GUO Rui-hua,ZHOU Chao-gang,et al. Study on dephosphorization of slag gasification in coke reduction converter[J]. Iron and Steel Vanadium and Titanium,2019,40(5):138.) [11] 佟帅,李晨晓,王书桓,等.钢渣处理工艺及综合利用分析[J].冶金能源,2020,39(06):3.(TONG Shuai,LI Chen-xiao,WANG Shu-huan,et al. Steel slag treatment process and comprehensive utilization analysis[J]. Energy for Metallurgical Industry,2020,39(6):3.) [12] 江露.Al2O3改性对中高磷转炉渣中磷富集行为的影响[C]//第十八届(2014年)全国炼钢学术会议. 西安:中国金属学会炼钢分会,2014.(JIANG Lu. Effect of Al2O3 modification on phosphorus accumulation in medium and high phosphorus converter slag[C]//The 18th(2014) National Conference on Steelmaking. Xi′an:Steelmaking Branch of the Chinese Society for Metals,2014.) [13] 潘晓亮,李晋岩,郭敏,等.二元碱度和Al2O3对CaO-SiO2-FeO-Fe2O3-P2O5-Al2O3-MgO-MnO钢渣中磷酸盐富集的影响[J].钢铁研究学报,2017,29(6):474.(PAN Xiao-liang,LI Jin-yan,GUO Min,et al. Effects of binary alkalinity and Al2O3 on CaO-SiO2-FeO-Fe2O3-P2O5-Al2O3-MgO-MnO phosphate enrichment in steel slag[J]. Journal of Iron and Steel Research,2017,29(6):474.) [14] 王达志,包燕平,王敏.高磷转炉渣中磷的富集行为研究[J].工程科学学报,2018,40(s1):65.(WANG Da-zhi,BAO Yan-ping,WANG Min. Research on the enrichment behavior of phosphorus in high phosphorus converter slag[J]. Journal of Engineering Science,2018,40(s1):65.) [15] 代献仁,刘军,张贤策.转炉渣中有价元素回收试验[J].现代矿业,2016,32(7):101.(DAI Xian-ren,LIU Jun,ZHANG Xian-ce. Recovery experiment of valuable elements in converter slag[J]. Modern Mining,2016,32(7):101.) [16] 姜琦,李猛.转炉渣磁选粉的工艺优化[J].山东工业技术,2015(13):34.(JIANG Qi,LI Meng. Process optimization of converter slag magnetic powder separation[J]. Shandong Industrial Technology,2015(13):34.) [17] 薛鹏,贺东风,徐安军,等.改质转炉渣中MgFe2O4的形成与磁选提铁[J].钢铁,2017,52(7):104.(XUE Peng,HE Dong-feng,XU An-jun,et al. Formation of MgFe2O4 in modified converter slag and magnetic separation for iron extraction[J]. Iron and Steel,2017,52(7):104.) [18] Numata M,Maruoka N,Kim S,et al. Fundamental experiment to extract phosphorous selectively from steelmaking slag by leaching[J]. ISIJ International,2014,54(8):1983. [19] Teratoko T,Maruoka N,Shibata H,et al. Dissolution behavior of dicalcium silicate and tricalcium phosphate solid solution and other phases of steelmaking slag in an aqueous solution[J]. High Temperature Materials and Processes,2012,31(4/5):329. [20] 谯勇.转炉钢渣浸出脱磷及含磷浸出液吸附除磷研究[D].重庆:重庆大学,2017.(QIAO Yong. Study on Dephosphorization of Converter Slag by Leaching and Removal of Phosphorus from Leach Liquor[D]. Chongqing:Chongqing University,2017.) [21] 王永红,谢兵,刁江,等.高磷铁水脱磷渣枸溶性[J].北京科技大学学报,2011,33(3):323.(WANG Yong-hong,XIE Bing,DIAO Jiang,et al. Solubility in citric acid of dephosphorization slags from high phosphorus hot metal refining[J]. Journal of University of Science and Technology Beijing,2011,33(3):323.) [22] 梁柱,李佳,李鹏,等.钢渣中钙镁离子的选择性浸出行为[J].中国冶金,2020,30(5):51.(LIANG Zhu,LI Jia,LI Peng,et al. Selective leaching behaviour of calcium and magnesium from steel slag[J]. China Metallurgy,2020,30(5):51.) [23] Zhang X,Atsumi H,Matsuura H,et al. Influence of gluconic acid on dissolution of Si,P and Fe from steelmaking slag with different composition into seawater[J]. ISIJ International,2014,54(6):1443. [24] Zhang X,Matsuura H,Tsukihashi F. Dissolution mechanism of various elements into seawater for recycling of steelmaking slag[J]. ISIJ International,2012,52(5):928. [25] 卫海英.SPSS在商务管理中的应用[M].北京:中国统计出版社,2010.(WEI Hai-ying. Application of SPSS in Business Management[M]. Beijing:China Statistics Press,2010.) [26] 曹玉茹,杨年华.基于SPSS最优尺度的回归方法[J].统计与决策,2019,35(12):72.(CAO Yu-ru,YANG Nian-hua. Regression method based on SPSS optimal scale[J]. Statistics and Decision,2019,35(12):72.)