Influence of Coiling Temperature and Total Cold Rolling Reduction Rate on Mechanical Properties of BContaining 08A1 Steel
KANG Yonglin1,JING Qinguang1,WU Guangliang2, WEN Dezhi2,ZHOU Chunquan 2
1. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China;2. Technical Center, Hunan Hualing Lianyuan Steel Co., Ltd., Loudi 417009, Hunan, China
Abstract:Bcontaining((40~60)×106,mass fraction) and Bfree 08Al hot strips produced by CSP process were used for experiment. The hot strips were coiled at different temperatures and then cold rolled with different reduction rate. After recrystallization annealing, the formability(rvalue and nvalue) and mechanical properties (YS,TS and A) were measured by tensile tests, in addition, two kinds of annealed sheets (coiling temperature 620 ℃;75% reduction) were analyzed by Xray diffraction(ODF) and electron backscattered diffraction (EBSD). The results showed that coiling temperature and total coldrolling reduction rate have remarkable influence on the formability and mechanical properties of Bcontaining and Bfree 08A1 steels after recrystallization annealing.ODF EBSD tests showed that the fraction of γfiber texture in Bcontaining steel is lower than that in Bfree steel, nevertheless, the rotating cubic texture ({001} <110>) and Goss texture ({011} <100>) are much more than that in Bfree steel.
康永林;景钦广;吴光亮;温德智;周春泉. 卷取温度、冷轧总变形量对含硼 08Al钢力学性能的影响[J]. 钢铁, 2007, 42(4): 67-0.
KANG Yonglin;JING Qinguang;WU Guangliang;WEN Dezhi;ZHOU Chunquan. Influence of Coiling Temperature and Total Cold Rolling Reduction Rate on Mechanical Properties of BContaining 08A1 Steel. Iron and Steel, 2007, 42(4): 67-0.