宝钢不锈钢AOD炉长寿技术
李冬刚
宝钢股份不锈钢分公司
the Longevity Technology of AOD Furnace in Baosteel
Dong-Gang LI
摘要 本文从炉壳型式、渣系组成、侧吹风枪选用等方面对宝钢AOD炉的长寿技术进步进行了介绍与分析,通过相关的研究与改进,宝钢AOD炉炉龄由投产初期的45炉/炉役提高至目前的185炉/炉役。
关键词 :
AOD炉 ,
不锈钢 ,
炉龄
Abstract :The improvements on the AOD furnace longevity technology are introduced and analyzed in this article from the shape of the shell, components of the slag and the selection on the side-blow tuyeres. Based on some works by the above, the campaign of the AOD was promoted from 45 heats to current 185 heats in Baosteel.
Key words :
argon oxygen decarburization furnace
stainless steel
campaign
收稿日期: 2009-08-10
[1]
魏统宇, 邹德宁, 张英波, 陈婉婉. 铝对高铝铁素体耐热钢组织与性能的影响 [J]. 钢铁, 2020, 55(6): 80-83.
[2]
李积武, 曹倩倩, 杨海茹. 冲击微动磨损条件下304不锈钢管道的变薄现象 [J]. 钢铁, 2020, 55(6): 118-122.
[3]
赵云鹏, 余超, 肖宏, 吴宗河, 许朋朋, 谢红飙. 纯铁中间层对热轧不锈钢复合板性能的影响 [J]. 钢铁, 2020, 55(5): 73-79.
[4]
吴翔宇, 何玉东, 吴良平, 沈平, 付建勋. 镁改质对Y1Cr13易切削不锈钢中硫化物的影响 [J]. 钢铁, 2020, 55(4): 68-74.
[5]
王欣, 潘建, 朱德庆, 郭正启, 田宏宇. 含镍、铬复合氧化球团的制备工艺 [J]. 钢铁, 2020, 55(3): 23-28.
[6]
马筱聪, 安子军, 陈雷, 梅瑞雪, 郝硕, 彭程. 加载方向对TRIP双相不锈钢板带拉伸性能的影响 [J]. 钢铁, 2020, 55(2): 112-118.
[7]
杨玉丹,赵洪山,刘腾轼,董瀚. 新型高碳马氏体不锈钢的组织与性能 [J]. 钢铁研究学报, 2020, 32(2): 135-142.
[8]
李玉峰1,2,唐兴昌3,潘吉祥1,2,王长波1,2. 904L不锈钢动态再结晶行为 [J]. 钢铁研究学报, 2020, 32(2): 159-165.
[9]
王国富, 余海峰. 特种金属及合金中厚板在线酸洗技术探讨 [J]. 物理测试, 2020, 38(1): 18-.
[10]
习小军, 杨树峰, 李京社, 赵梦静, 叶茂林. 含铈304不锈钢夹杂物改性及耐腐蚀性能优化 [J]. 钢铁, 2020, 55(1): 20-26.
[11]
宜亚丽, 韩晓铠, 张磊, 金贺荣. 316L/EH40不锈钢复合板热轧过程中晶粒组织的均匀性 [J]. 钢铁, 2020, 55(1): 47-55.
[12]
管真, 孙永庆, 李莉, 田帅, 刘振宝, 梁剑雄. 冶炼工艺对15-5PH不锈钢疲劳性能的影响 [J]. 钢铁, 2020, 55(1): 72-80.
[13]
杨吉春, 王军, 任磊, 富晓阳, 刘香军, 张泽宁. 铈对S32550双相不锈钢微观组织及冲击性能的影响 [J]. 钢铁, 2020, 55(1): 86-92.
[14]
高祥明,裴明德,李国平. 冷轧硬化对超级双相不锈钢S32750析出相的影响 [J]. 钢铁, 2019, 54(9): 94-98.
[15]
曾建华,张敏,吴国荣,谢鑫. 30Cr13不锈钢冶炼过程夹杂物控制技术 [J]. 钢铁, 2019, 54(8): 43-47.