Formation Mechanism and Control of Transverse Corner Cracking of Containing Boron Steel Slab
WANG Zhao-yang1,2,JI Cheng1,GONG Wen-xu2,ZHU Miao-yong1
1. School of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China 2. Tianjin Iron and Steel Co., Ltd., Tianjin 300301, China
Abstract:The optical microscope and SEM were applied to analyze the formation mechanism of transverse corner cracks of boron micro-alloyed steel slab. It is found that the cracks occur at relatively low corner temperatures of slab in straightening section that is in No.3 brittle zone of boron steel firs. The corner temperature of slab is relatively low due to the relatively low casting speed, irrational distribution of secondary cooling water and sprayers. Increasing casting speed and decreasing the cooling water flux at slab corners in the straightening section for mild cooling were performed first to control corner temperature above the upper limit in No.3 brittle zone of boron steel. Combined with the adjustment of dynamic, as a result, the corner temperature of slab was increased apparently, transverse corner cracking and internal quality of slab was greatly improved.
王朝阳,,祭程,巩文旭,朱苗勇. 含硼钢板坯边角裂纹的成因与控制[J]. 钢铁, 2012, 47(5): 35-38.
WANG Zhao-yang1,2,JI Cheng1,GONG Wen-xu2,ZHU Miao-yong1. Formation Mechanism and Control of Transverse Corner Cracking of Containing Boron Steel Slab. Iron and Steel, 2012, 47(5): 35-38.
Akihiko K.Mechanism of the Internal Oxidation Layer Along the surface crack on the slab[J]. Tetsu—to—Hagane, 1995, 81(1): 52.
[1]
Akihiko K.Mechanism of the Internal Oxidation Layer Along the surface crack on the slab[J]. Tetsu—to—Hagane, 1995, 81(1): 52.
[2]
Akihiko K.Estimation of the Formed Position of the Surface cracks on the slab in the continuous Caster[J]. TETSU—TO—HAGANE, 1996, 82(1): 35.
[2]
Akihiko K.Estimation of the Formed Position of the Surface cracks on the slab in the continuous Caster[J]. TETSU—TO—HAGANE, 1996, 82(1): 35.
[3]
Mintz B. Influence of composition on the Hot Ductility of steels and the Problem of Transverse cracking[J].Isij International,1999,39(9):833.
[3]
Mintz B. Influence of composition on the Hot Ductility of steels and the Problem of Transverse cracking[J].Isij International,1999,39(9):833.
[4]
Mintz B.Hot-Ductility Behavior of c-Mn-Nb-A1 steels and Its Relationship to Crack Propagation During the Straightening of continuously cast strand[J].Metals Technology,1979,(1):24.
[4]
Mintz B.Hot-Ductility Behavior of c-Mn-Nb-A1 steels and Its Relationship to Crack Propagation During the Straightening of continuously cast strand[J].Metals Technology,1979,(1):24.