Effects of Finish Rolling Temperature on Microstructure and Properties in Nb-Ti Low Alloying Bainite Steel
CAO Li-chao1, YU Hong-wei1, WANG Shi-sen2, LI De-fa2
1. Technology Center, Wuhan Iron and Steel Group Echeng Iron and Steel Co., Ltd., Ezhou 436002, Hubei, China 2. Research and Development Center of Wuhan Iron and Steel Group, Wuhan 430080, Hubei, China)
Abstract:The effects of finish rolling temperature on microstructures and properties were investigated in TMCP (thermo-mechanical controlled processing) bainite steel using optical microscope, transmission electron microscope, EDS analysis and mechanical testing equipments. The results show that strength and toughness improve respectively as finish rolling temperature decrease. A lot of proeutectiod ferrite grains form along boundaries and strength and toughness of steel plate decreases after finish rolling at 815 ℃ with the reason of temperature drop into austenite and ferrite double phases zone before accelerate cooling. Excellent properties can be obtained by finish rolling temperature is 870 ℃. Yield and tensile strength are 805 MPa and 1 005 MPa respectively. Average charpy impact energy is 197 J. The microstructures are bainite, martensite and Nb-Ti contained dispersive precipitates with the size of 30-50 nm.
收稿日期: 2013-09-13
出版日期: 2014-06-11
引用本文:
曹立潮, 余宏伟, 王世森, 李德发. 终轧温度对低合金铌钛贝氏体钢组织和性能的影响[J]. 钢铁, 2014, 49(6): 65-68.
CAO Li-chao, YU Hong-wei, WANG Shi-sen, LI De-fa. Effects of Finish Rolling Temperature on Microstructure and Properties in Nb-Ti Low Alloying Bainite Steel. Iron and Steel, 2014, 49(6): 65-68.
David Porter,Anssi Laukkanen,etc.Performance of TMCP steel with respect to mechanical properties after cold forming and post-forming heat treatment[J].International Journal of Pressure Vessels and Piping,2004,81:867-
[2]
David Porter,Anssi Laukkanen,etc.Performance of TMCP steel with respect to mechanical properties after cold forming and post-forming heat treatment[J].International Journal of Pressure Vessels and Piping,2004,81:867-