Effect of heat treatment technology on reversed austenite in super martensitic stainless steel
JIANG Wen1, ZHAO Kun-yu1, YE Dong1, LI Jun1, SU Jie2, YONG Qi-long2
1. College of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, Yunnan, China 2. Department of Structural Materials, Central Iron and Steel Research Institute,
Abstract:Beijing 100081, China) The effect of adding different content of Cr to the super martensitic stainless steel (SMSS) on formation of reversed austenite subjected to quenching and tempering by using optical microscope(OM), X-ray diffraction (XRD), transmission electron microscope (TEM) and energy dispersive spectrometer(EDS) was studied. The experimental results indicate that the microstructures of two tested steels were tempered martensite and reversed austenite after tempering. The volume fraction and grain size of reversed austenite in two tested steels increased first and then decreased with the increase of tempering temperature, which reached the maximum at 650-700 ℃. When the reversed austenite re-dissolved and transformed to martensite, there was an effect of refinement on the matrix. Compared with 13Cr steels, the reversed austenite in 15Cr steels was more and the size was bigger. The effect of refinement on the matrix was more obvious.
收稿日期: 2014-04-15
出版日期: 2015-02-02
引用本文:
姜雯,赵昆渝,业冬,李俊,苏杰,雍岐龙. 热处理工艺对超级马氏体钢逆变奥氏体的影响[J]. 钢铁, 2015, 50(2): 70-75.
JIANG Wen, ZHAO Kun-yu, YE Dong, LI Jun, SU Jie, YONG Qi-long. Effect of heat treatment technology on reversed austenite in super martensitic stainless steel. Iron and Steel, 2015, 50(2): 70-75.
C.A.D. Rodrigues, P.L.D. Lorenzo, A. Sokolowski, C.A. Barbosa, J.M.D.A. Rollo. Development of a Supermartensitic Stainless Steel Microalloyed with Niobium[J]. J ASTM, 2006, (3): 1-5.
[1]
C.A.D. Rodrigues, P.L.D. Lorenzo, A. Sokolowski, C.A. Barbosa, J.M.D.A. Rollo. Development of a Supermartensitic Stainless Steel Microalloyed with Niobium[J]. J ASTM, 2006, (3): 1-5.
[2]
De-ning ZOU, Ying HAN, Wei ZHANG, Xu-dong FANG. Influence of tempering process on mechanical properties of 00Cr13Ni4Mo supermartensitic stainless steel[J]. Journal of Iron and Steel Research, 2010, (17): 50-54.
[2]
De-ning ZOU, Ying HAN, Wei ZHANG, Xu-dong FANG. Influence of tempering process on mechanical properties of 00Cr13Ni4Mo supermartensitic stainless steel[J]. Journal of Iron and Steel Research, 2010, (17): 50-54.
[3]
Linne CP, Blanchard F, Guntz GC, Orlans-Joliet BJ. Corrosion performances of modified 13Cr for OCTG in oil and gas environments[J]. Corrosion, 1997, (97): 9-20.
[3]
Linne CP, Blanchard F, Guntz GC, Orlans-Joliet BJ. Corrosion performances of modified 13Cr for OCTG in oil and gas environments[J]. Corrosion, 1997, (97): 9-20.
[4]
P.D. Bilmes, M. Solari, C.L. Llorente. Characteristics and effects of austenite resulting from tempering of 13Cr-NiMo martensitic steel weld metals[J].Materials Characterization, 2001, (46): 285-296.
[4]
P.D. Bilmes, M. Solari, C.L. Llorente. Characteristics and effects of austenite resulting from tempering of 13Cr-NiMo martensitic steel weld metals[J].Materials Characterization, 2001, (46): 285-296.
[5]
Hubackova J, Cihal V, Mazanec K. Two-Stage Tempering of steel 13%Cr6%Ni[J]. Materialwissenschaft und Werkstofftechnik, 1984, (15): 411-415.
[5]
Hubackova J, Cihal V, Mazanec K. Two-Stage Tempering of steel 13%Cr6%Ni[J]. Materialwissenschaft und Werkstofftechnik, 1984, (15): 411-415.
[6]
D. J. Dyson, B. Holmes. Effect of alloying additions on the lattice parameter of austenite[J]. Iron and Steel Institute of Japan. 1970, (208): 469-474.
[6]
D. J. Dyson, B. Holmes. Effect of alloying additions on the lattice parameter of austenite[J]. Iron and Steel Institute of Japan. 1970, (208): 469-474.
[7]
F C Monkman, F B Cuff, N. J. Grant. Computation of Ms for stainless steels[J]. Metals Progress. 1957, (71): 94-96.
[7]
F C Monkman, F B Cuff, N. J. Grant. Computation of Ms for stainless steels[J]. Metals Progress. 1957, (71): 94-96.
[8]
G H Eichelman, F. C. Hull. The effect of composition on the temperature of spontaneous transforamtion of austenite or martensite in 18-8 type stainless steel[J]. Transactions of the ASM. 1953, (45): 77-104.
[8]
G H Eichelman, F. C. Hull. The effect of composition on the temperature of spontaneous transforamtion of austenite or martensite in 18-8 type stainless steel[J]. Transactions of the ASM. 1953, (45): 77-104.