Influence of cooling process on the phase transformation and microstructure of HRB400E
CHEN Bo-yu1, LIAO Lin-lin1, WANG Ming-di1, MENG Xiang2, LI Hui2, CHEN Yin-li2
(1. Technical Center, Fujian Sanming Iron and Steel Group, Sanming 365000, Fujian, China 2. Metallurgy Engineering Research Institute, University of Science and Technology Beijing, Beijing 100083, China)
Abstract:The microstructure of HRB400E was decided by the cooling process after laying. The different cooling processes were simulated by Gleeble-3500 thermal simulation tester. The dilatometric curve and microstructure were analyzed under different cooling processes. The results indicate that the cooling rate and mutational temperature greatly influenced the final microstructure. The rational cooperation of these two parameters could dominate the fraction of bainite. With the increasing of cooling rate and decreasing of mutational temperature,the fraction of bainite enhanced.
陈伯瑜,廖琳琳,王明娣,孟祥,李辉,陈银莉. 分段冷却对HRB400E相变过程及微观组织的影响[J]. 钢铁, 2015, 50(2): 81-84.
CHEN Bo-yu, LIAO Lin-lin, WANG Ming-di, MENG Xiang, LI Hui, CHEN Yin-li. Influence of cooling process on the phase transformation and microstructure of HRB400E. Iron and Steel, 2015, 50(2): 81-84.