Abstract：The mechanical properties of experimental AF1410 with 30% Mo aged at different temperature were studied. The results indicated that the experimental steel has obvious effects of secondary hardening with a age hardening peak at 460 ℃,and the hardness was higher than that of original AF1410 steel by 15 HRC.
李阿妮;厉勇;王春旭;刘宪民. Mo含量对AF1410钢二次硬化效果的影响[J]. 钢铁, 2007, 42(9): 60-0.
LI Ani;LI Yong;WANG Chunxu;LIU Xianmin. Influence of Mo on Secondary Hardening Behavior of UltraHigh Strength AF1410 Steel. Iron and Steel, 2007, 42(9): 60-0.
2007, Vol. 42 