Effect of hot-rolled coiling temperature on microstructure,properties and textures of micro-carbon deep-drawing DP steel
YE Jie-yun1,AN Gui-huan1, LIU Shan-shan1,LIU Wei-ning2,WANG Zhi-gang1
(1. School of Material Science and Engineering,Jiangxi University of Science and Technology,Ganzhou 341000,Jiangxi,China 2. AC Construction Branch,State Grid Corporation of China,Beijing 100031,China)
Abstract:In order to study the charge rule of texture on deep-drawing DP steel, effect of hot-rolled coiling temperature on microstructure, properties and textures of micro-carbon deep drawing DP steel were studied by OM,TEM and XRD technical. The research shows that: microstructure of hot-rolled plates is mainly composed of ferrite and pearlite. With the increasing of coiling temperature, the grain size of ferrite increased slightly, and elongation of hot-rolled plate enhanced gradually. The optimum precipitation temperature of Mo-based carbide in hot-rolled plate is 700 ℃. A higher volume fraction (4%) of martensite and finer (11.7 μm) ferrite observed in annealed sheet on 700 ℃ coiling compared with 650 and 750 ℃. Meanwhile, the strongest 〈111〉//ND fiber texture and weakest {001}〈110〉 texture achieved in annealed sheet. The tensile strength and r value of annealed sheet on 700 ℃ coiling reach to 455 MPa and1.5, respectively.
叶洁云,安桂焕,刘姗姗,刘蔚宁,汪志刚. 卷取温度对深冲DP钢组织性能及织构的影响[J]. 钢铁, 2016, 51(12): 73-79.
YE Jie-yun,AN Gui-huan, LIU Shan-shan,LIU Wei-ning,WANG Zhi-gang. Effect of hot-rolled coiling temperature on microstructure,properties and textures of micro-carbon deep-drawing DP steel. Iron and Steel, 2016, 51(12): 73-79.